Formation and Control of CaS Inclusion in Gear Steel 20MnCr5

被引：2
|
作者：
Xu, Jie [1 ]
Fu, Jianxun [1 ]
Wu, Yanxin [1 ]
Li, Xu [1 ]
机构：
[1] Shanghai Univ, Sch Mat Sci & Engn, Shanghai Key Lab Adv Ferromet, State Key Lab Adv Special Steel, Shanghai, Peoples R China
来源：
TMS 2017 146TH ANNUAL MEETING & EXHIBITION SUPPLEMENTAL PROCEEDINGS | 2017年
基金：
中国国家自然科学基金;
关键词：
20MnCr5; Calcium treatment; Thermodynamics; Nozzle clogging;
D O I：
10.1007/978-3-319-51493-2_40
中图分类号：
TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
The modification of (CaO)m(Al2O3)n inclusion and the fact of CaS inclusion formation in gear steel 20MnCr5 after calcium treatment have been studied by thermodynamic equilibrium calculation. Based on the thermodynamic equilibrium, when the liquid steel containing 0.035% [Al], the mass fraction of sulfur is lower than 0.00628% and the ratio of w(Ca)/w(Al) is higher than 0.483, the lower melting point 12(CaO) center dot 7(Al2O3) inclusion will form in the molten steel. Calculated results show that with calcium treatment of liquid steel the stable CaS forms easily and the aluminum deoxidizing product Al2O3 is easily modified to low-melting calcium aluminate 12(CaO) center dot 7(Al2O3). In order to completely modify the Al2O3 to low-melting calcium aluminate (CaO) center dot (Al2O3) and 12(CaO) center dot 7(Al2O3), the calcium treatment of liquid steel should carry out in conditions of low [S] and >= 1600 C-omicron, and the sulfur wire feeding operation after soft argon stirring in refining process, it is available to obviously decrease the occurrence of nozzle blocking.
引用
收藏
页码：425 / 433
页数：9
相关论文
共 50 条
  • [41] Experimental and numerical study of contact fatigue for 18CrNiMo7-6 and 20MnCr5 carburized gear tooth
    Calabokis, Oriana Palma
    Nunez de la Rosa, Yamid Enrique
    de Moraes, Samara Paulin
    Antunes, Estela Vicentim
    Cousseau, Tiago
    da Silva, Carlos Henrique
    SURFACE TOPOGRAPHY-METROLOGY AND PROPERTIES, 2022, 10 (03)
  • [42] 20MnCr5齿轮钢全流程夹杂物分析
    白旭旭
    张敏
    曾建华
    杨树峰
    李京社
    钢铁钒钛, 2022, 43 (06) : 143 - 148
  • [43] 20MnCr5圆棒锯切困难原因分析
    陆伟成
    廖美华
    杨雄强
    杨明梅
    物理测试, 2021, 39 (04) : 47 - 50
  • [44] Comparison of slip-rolling behaviour between 20MnCr5 gear steel, 36NiCrMoV1-5-7 hot working tool steel and 45SiCrMo6 spring steel
    Burbank, John
    Woydt, Mathias
    WEAR, 2015, 328 : 28 - 38
  • [45] 20MnCr5钢中马氏体回火的EBSD研究
    王申存
    吴益文
    华沂
    李志成
    张鸿
    材料热处理学报, 2011, 32 (01) : 43 - 48
  • [46] Distortion measurements of cylindrical 20MnCr5 discs during quenching in oil
    Stöbener, D.
    Acht, C.
    Zoch, H.-W.
    Goch, G.
    HTM - Haerterei-Technische Mitteilungen, 2007, 62 (04): : 157 - 162
  • [47] Distortion formation in forged disks made of 20MnCr5 - Inluence of hot-forming and material structure
    Rentsch, R.
    HTM-JOURNAL OF HEAT TREATMENT AND MATERIALS, 2012, 67 (05): : 323 - 330
  • [48] Distortion control in 20MnCr5 bevel gears after liquid nitriding process to maintain precision dimensions
    Mahendiran, M.
    Kavitha, M.
    INTERNATIONAL CONFERENCE ON ADVANCES IN METALLURGY, MATERIALS AND MANUFACTURING, 2018, 314
  • [49] 真空冶炼对20MnCr5钢疲劳性能的影响
    潘一凡
    袁文
    林业机械与木工设备, 2002, (10) : 24 - 26
  • [50] A Comparative Study of Kinetic Models Regarding Bainitic Transformation Behavior in Carburized Case Hardening Steel 20MnCr5
    Damon, J.
    Muehl, F.
    Dietrich, S.
    Schulze, V.
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2019, 50A (01): : 104 - 117
12345