The effect of mechanical load on transport property and pore structure of alkali-activated slag concrete

被引:38
作者
Zhang, Yu [1 ]
Wan, Xiaomei [1 ]
Hou, Dongshuai [1 ]
Zhao, Tiejun [1 ]
Cui, Yifei [1 ]
机构
[1] Qingdao Univ Technol, Sch Civil Engn, Qingdao, Peoples R China
基金
中国国家自然科学基金;
关键词
Alkali-activated slag concrete; Pore structure; Transport property; Shrinkage microcracks; Compressive load; BLAST-FURNACE SLAG; FLY-ASH; CHLORIDE PERMEABILITY; GAS-PERMEABILITY; WATER-GLASS; STRENGTH; MORTARS; DURABILITY; HYDRATION; SHRINKAGE;
D O I
10.1016/j.conbuildmat.2018.09.009
中图分类号
TU [建筑科学];
学科分类号
0813 ;
摘要
It would make sense to detect the rules and mechanisms of degradation and mass transport of alkali activated slag concrete (AASC) in actual service environment. In this paper, hydration products characterization implies higher crystallinity degree of C-S-H activated by NaOH and higher polymerization of the one activated by water glass. During compressive loading, Poisson's ratio of AASC keeps constant at the stress level ranging from 0 to 0.5, with an uprush takes place at stress level of 0.8-0.9. For slag concrete activated by NaOH, volume increases with stress level, while the volume of slag concrete activated by water glass decreases first and then increase with stress level. The apparent chloride diffusion coefficient of specimens activated by NaOH is 4-7 times smaller than the ones activated by water glass, which is verified by the results that volume of pores above 10 gm of water glass activated sample is nearly 20 times more than that of NaOH activated one. Slag concrete activated by water glass is compacted considerably by compressive loading contributing to the decrease in chloride diffusivity, while no significant compacting phenomenon is observed in slag concrete activated by NaOH. However, there is no significant compacting effect on capillary absorption for both specimens activated by two activators. (C) 2018 Elsevier Ltd. All rights reserved.
引用
收藏
页码:397 / 408
页数:12
相关论文
共 41 条
[1]   Durability of concrete incorporating GGBS activated by water-glass [J].
Al-Otaibi, Saud .
CONSTRUCTION AND BUILDING MATERIALS, 2008, 22 (10) :2059-2067
[2]   Influence of activator on the strength and drying shrinkage of alkali-activated slag mortar [J].
Atis, Cengiz Duran ;
Bilim, Cahit ;
Celik, Oezlem ;
Karahan, Okan .
CONSTRUCTION AND BUILDING MATERIALS, 2009, 23 (01) :548-555
[3]  
Banthia N, 2007, ACI MATER J, V104, P70
[4]   Influence of activator type on hydration kinetics, hydrate assemblage and microstructural development of alkali activated blast-furnace slags [J].
Ben Haha, M. ;
Le Saout, G. ;
Winnefeld, F. ;
Lothenbach, B. .
CEMENT AND CONCRETE RESEARCH, 2011, 41 (03) :301-310
[5]   Engineering and durability properties of concretes based on alkali-activated granulated blast furnace slag/metakaolin blends [J].
Bernal, Susan A. ;
Mejia de Gutierrez, Ruby ;
Provis, John L. .
CONSTRUCTION AND BUILDING MATERIALS, 2012, 33 :99-108
[6]   Sodium silicate-based, alkali-activated slag mortars Part I. Strength, hydration and microstructure [J].
Brough, AR ;
Atkinson, A .
CEMENT AND CONCRETE RESEARCH, 2002, 32 (06) :865-879
[7]   Residual strength and pore structure of high-strength concrete and normal strength concrete after exposure to high temperatures [J].
Chan, YN ;
Peng, GF ;
Anson, M .
CEMENT & CONCRETE COMPOSITES, 1999, 21 (01) :23-27
[9]   Effects and interactions of temperature and stress-level related damage on permeability of concrete [J].
Choinska, Marta ;
Khelidj, Abdelhafid ;
Chatzigeorgiou, George ;
Pijaudier-Cabot, Gilles .
CEMENT AND CONCRETE RESEARCH, 2007, 37 (01) :79-88
[10]  
Fagerlund G., 1982, NORD CONCR RES, V1