Effect of Co2+ Ions Doping on the Structural and Optical Properties of Magnesium Aluminate

Cobalt-doped nanosized magnesium aluminate (Mg1-xCoxAl2O4) samples having different compositions (x = 0.2, 0.4, 0.6, 0.8, 1.0) were synthesized by a chemical co-precipitation method. All samples were characterized by means of x-ray diffraction (XRD), scanning electron microscopy, Fourier transform infrared spectroscopy, ultra violet-visible spectroscopy, photoluminescence and diffused reflectance spectroscopy. The results of XRD revealed that the samples were spinel single phase cubic close packed crystalline materials. The lattice constant and x-ray density were found to be affected by the ionic radii of the doped metal cations. Using the Debye-Scherrer formula, the calculated crystalline size was found to be Co2+ ion concentration-dependent and varied between 32 nm and 40 nm. Nano-dimensions and phase of the Mg1-xCoxAl2O4 samples were analyzed and the replacement of Mg2+ ions with Co2+ ions was confirmed by elemental analysis. Three strong absorption bands at 540 nm, 580 nm and 630 nm were observed for the doped samples which are attributed to the three spin-allowed T-4(1g) (F-4) -> T-4(2g), (4)A(2g), T-4(1g) (4P) electronic transitions of Co2+ at tetrahedral lattice sites. Nanophosphors have optical properties different from bulk because of spatial confinement and non-radiative relaxation. Decreases in particle size can increase the surface area and the defects, which can in turn increase the luminescent efficiency to make it very useful for tunable laser operations, persistent phosphorescence, color centers, photoconductivity and luminescence for display technology. MgAl2O4 was doped with Co2+ ions using a co-precipitation method and the optical absorption studies revealed that there is a decrease of band gap due to the increase of Co2+ content. The emission intensity of this phosphor is observed at 449 nm with a sharp peak attributed to the smaller size of the particles and the homogeneity of the powder.