Manganese distribution between FeO-MnO-SiO2-CaO-MgO-Al2O3 slags and molten iron

Pretreatment of high manganese hot metal is suggested to produce hot metal suitable for further processing to steel in conventional LD converter and rich manganese slags satisfy the requirements for the production of silicomanganese alloys. Manganese distribution between slag and iron represents the efficiency of manganese oxidation from hot metal. The present study has been done to investigate the effect of temperature, slag basicity and composition of oxidizer mixture on the distribution coefficient of manganese between slag and iron. Ferrous oxide activity was determined in molten synthetic slag mixtures of FeO-MnO-SiO2-CaO-MgO-Al2O3. The investigated slags had chemical compositions similar to either oxidizer mixture or slags expected to result from the treatment of high manganese hot metal. The technique used to measure the ferrous oxide activity in the investigated slag systems was the well established one of gas-slag-metal equilibration in which molten slags contained in armco iron crucibles are exposed to a flowing gas mixture with a known oxygen potential until equilibrium has been attained. After equilibration, the final chemical analysis of the slags gave compositions having a particular ferrous oxide activity corresponding to the oxygen potential of the gas mixture. The determined values of ferrous oxide activity were used to calculate the equilibrium distribution of manganese between slag and iron. Higher manganese distribution between slag and iron was found to be obtained by using oxidizer containing high active iron oxide under acidic slag and relatively low temperature of about 1350degreesC.