A study of ageing effect: Migration of rhodium under air atmosphere

被引：6

作者：

Tomida, Yasutaka ^{[1
]}

Haneda, Masaaki ^{[1
,2
]}

机构：

[1] Nagoya Inst Technol, Adv Ceram Res Ctr, 10-6-29 Asahigaoka, Tajimi, Gifu 5070071, Japan

[2] Nagoya Inst Technol, Frontier Res Inst Mat Sci, Showa Ku, Gokiso Cho, Nagoya, Aichi 4658555, Japan

来源：

CATALYSIS TODAY | 2021年 / 376卷

关键词：

Rh migration; Rh catalyst; Three-way catalyst; Ageing; OXYGEN STORAGE CAPACITY; 3-WAY CATALYSTS; SUPPORT INTERACTION; RH; REDUCTION; CERIA; ZRO2; PLATINUM; NO; CO;

D O I：

10.1016/j.cattod.2020.07.083

中图分类号：

O69 [应用化学];

学科分类号：

081704 ;

摘要：

Rh is the most important element for the current TWC technology. However, the deterioration of Rh is occurred during the high-temperature ageing under an air condition, leading to Rh migration. From the EPMA results, the migration of Rh was found to really take place, resulting in the formation of new Rh - support interaction. This was also supported by the formation of RhAlOx on the catalyst surface, which was confirmed by XPS, in the aged "Rh/CZ + Al" sample. Although Rh/CZ showed higher NO reduction than Rh/Al under dynamic conditions, "Rh/ CZ + Al" and "Rh/Al + CZ" after high-temperature ageing showed similar NO reduction performance, which seems to be a sum of the activity of Rh/CZ and Rh/Al. This was explained by the Rh migration. The results of H2TPR and FT-IR spectroscopy following CO adsorption revealed that many of Rh particles are still present on CZ even after the high-temperature ageing because of Rh - CZ interaction.

引用

页码：81 / 86

页数：6

共 45 条

[1]

[Anonymous], 2009, Toyota Motor Corp J.P., Patent No. [2009-285606 A, 2009285606]

[2] STEAM EFFECTS IN 3-WAY CATALYSIS [J].

BARBIER-JR, J ;

DUPREZ, D .

APPLIED CATALYSIS B-ENVIRONMENTAL, 1994, 4 (2-3) :105-140

[3] Improved activity and durability of Rh-based three-way catalyst under diverse aging atmospheres by ZrO2 support [J].

Cao, Yidan ;

Ran, Rui ;

Wu, Xiaodong ;

Zhao, Baohuai ;

Weng, Duan .

JOURNAL OF ENVIRONMENTAL SCIENCES, 2017, 52 :197-203

[4] Ageing resistance of rhodium supported on CeO2-ZrO2 and ZrO2: Rhodium nanoparticle structure and Rh-support interaction under diverse ageing atmosphere [J].

Cao, Yidan ;

Ran, Rui ;

Wu, Xueyuan ;

Wu, Xiaodong ;

Wan, Jie ;

Weng, Duan .

CATALYSIS TODAY, 2017, 281 :490-499

[5] The physical chemistry and materials science behind sinter-resistant catalysts [J].

Dai, Yunqian ;

Lu, Ping ;

Cao, Zhenming ;

Campbell, Charles T. ;

Xia, Younan .

CHEMICAL SOCIETY REVIEWS, 2018, 47 (12) :4314-4331

[6] Rhodium dispersion during NO/CO conversions [J].

Dent, Andrew J. ;

Evans, John ;

Fiddy, Steven G. ;

Jyoti, Bhrat ;

Newton, Mark A. ;

Tromp, Moniek .

ANGEWANDTE CHEMIE-INTERNATIONAL EDITION, 2007, 46 (28) :5356-5358

[7] Oxygen storage capacity measurements of three-way catalysts under transient conditions [J].

Descorme, C ;

Taha, R ;

Mouaddib-Moral, N ;

Duprez, D .

APPLIED CATALYSIS A-GENERAL, 2002, 223 (1-2) :287-299

[8]

Di Monte R, 2004, TOP CATAL, V28, P47

[9]

ENGLER B, 1991, STUD SURF SCI CATAL, V71, P641, DOI 10.1016/S0167-2991(08)63008-6

[10] Ce1-xRhxO2-δ solid solution formation in combustion-synthesized Rh/CeO2 catalyst studied by XRD, TEM, XPS, and EXAFS [J].

Gayen, A ;

Priolkar, KR ;

Sarode, R ;

Jayaram, V ;

Hegde, MS ;

Subbanna, GN ;

Emura, S .

CHEMISTRY OF MATERIALS, 2004, 16 (11) :2317-2328

← 1 2 3 4 5 →