Study of the effect of hyperbranched polyols on cationic UV curable coating properties

被引:30
|
作者
Chen, Zhigang [1 ]
Webster, Dean C. [1 ]
机构
[1] N Dakota State Univ, Dept Coatings & Polymer Mat, Ctr Nanoscale Sci & Engn, Fargo, ND 58105 USA
关键词
hyperbranched; polyol; cationic photopolymerization; coating; inhomogeneity;
D O I
10.1002/pi.2202
中图分类号
O63 [高分子化学(高聚物)];
学科分类号
070305 ; 080501 ; 081704 ;
摘要
Cycloaliphatic epoxide-based cationic UV curable coatings containing three different hyperbranched polyols (HBPs) were systematically formulated and characterized. Polyether polyols were found to deter epoxide conversion under low UV intensity. For high UV intensity, the cycloaliphatic epoxide conversion increased with polyol content. Coatings with HBPs had better flexibility and solvent resistance than those containing a reference triol. Compared to the triol and polyester HBPs, polyether HBPs imparted lower T-g and hardness but a better flexibilizing effect to the coatings. At higher R values, the coating solvent resistance decreased except for those with one polyether HBP. A two-peak phenomenon was discovered in the residual thermal reaction heat curve after photoDSC experiments. These two peaks were found to be related to the thermal relaxation behavior of the photocured inhomogeneous film, and the reactivation and reaction of the 'trapped living cationic species'. The capability of the polyol to lower the high-temperature-peak temperature corresponded well with the flexibilizing ability. (c) 2006 Society of Chemical Industry
引用
收藏
页码:754 / 763
页数:10
相关论文
共 50 条
  • [31] Nanomechanical characterization of UV curable hyperbranched polymers
    Kim, J.
    Chen, Z.
    Chisholm, B.
    Patel, S.
    NSTI NANOTECH 2008, VOL 1, TECHNICAL PROCEEDINGS: MATERIALS, FABRICATION, PARTICLES, AND CHARACTERIZATION, 2008, : 936 - +
  • [32] UV-curable coating
    Mejiritski, M
    PHOTONICS SPECTRA, 2002, 36 (01) : 98 - 98
  • [33] UV-curable hyperbranched nanocomposite coatings
    Fogelström, L
    Antoni, P
    Malmström, E
    Hult, A
    PROGRESS IN ORGANIC COATINGS, 2006, 55 (03) : 284 - 290
  • [34] Synthesis and UV-curable Study of Dendritic Hyperbranched Methacrylate Coatings
    Zhang, Linya
    Liu, Fangfang
    PROCEEDINGS OF THE 2013 INTERNATIONAL CONFERENCE ON MATERIAL SCIENCE AND ENVIRONMENTAL ENGINEERING (MSEE 2013), 2013, : 239 - 243
  • [35] Study on photoinitiator in UV curable powder coating.
    Wei, J
    Wang, YM
    Sun, ZY
    ABSTRACTS OF PAPERS OF THE AMERICAN CHEMICAL SOCIETY, 2003, 225 : U712 - U712
  • [36] Preparation and properties of UV-curable hyperbranched polyurethane acrylate hard coatings
    Fu, Junchao
    Yu, Haojie
    Wang, Li
    Lin, Long
    Khan, Rizwan Ullah
    PROGRESS IN ORGANIC COATINGS, 2020, 144
  • [37] Synthesis and properties of hyperbranched polythioether modified epoxy acrylate UV curable coatings
    Qian J.-Y.
    Li P.
    Wei W.
    Liu X.-Y.
    Li X.-J.
    Surface Technology, 2021, 50 (07): : 337 - 344
  • [38] Hyperbranched polymers in cationic UV curing
    Sangermano, M.
    Amerio, E.
    Di Gianni, A.
    Priola, A.
    Pospiech, D.
    Voit, B.
    MACROMOLECULAR SYMPOSIA, 2007, 254 : 9 - 15
  • [39] Synthesis and curing behaviors of UV curable hyperbranched polysiloxane
    Si, QF
    Fan, XD
    Wang, X
    Wang, SJ
    ACTA POLYMERICA SINICA, 2005, (06) : 947 - 952
  • [40] Synthesis and characterization of UV curable hyperbranched poly(siloxyselane)
    Wang Shengjie
    Fan Xiaodong
    Kong Jie
    Wang Xin
    Zhang Guobin
    ACTA POLYMERICA SINICA, 2006, (08) : 1024 - 1028