Performance of corrosion protection of carbon steel with cerium modified phosphate-permanganate coatings and a layer of silane doped with cerium

被引：0

作者：

Girciene, O. ^{[1
]}

Gudaviciute, L. ^{[1
]}

Martusiene, A. ^{[1
]}

Jasulaitiene, V. ^{[1
]}

Selskiene, A. ^{[1
]}

Ramanauskas, R. ^{[1
]}

机构：

[1] Ctr Phys Sci & Technol, 3 Sauletekio Ave, LT-10257 Vilnius, Lithuania

来源：

CHEMIJA | 2019年 / 30卷 / 03期

关键词：

corrosion protection; self-healing; phosphate-permanganate; cerium; silane; SOL-GEL COATINGS; AZ31 MAGNESIUM ALLOY; CONVERSION COATINGS; PRETREATMENTS; RESISTANCE; CHROMATE; FILMS; INHIBITION; BEHAVIOR;

D O I：

暂无

中图分类号：

O6 [化学];

学科分类号：

0703 ;

摘要：

This work was aimed to evaluate the effect of bis-[triethoxysilylpropyl] tetrasulfide (BTESPT) doped with cerium nitrate, as a corrosion inhibitor, on improved corrosion resistance of samples of carbon steel with a phosphate-permanganate layer in a 0.5 M NaCl solution. The main goal of the present work was to compare self-healing capacities of cerium conversion coatings and cerium as an additive inhibitor to silane. The composition and structure of the investigated samples were characterized by scanning electron microscope (SEM) and X-ray photoelectron spectroscopy (XPS) techniques, while the corrosion behaviour was investigated applying voltametric and electrochemical impedance spectroscopy (EIS) measurements. The results of EIS measurements performed during 24 h immersion of the investigated samples into the 0.5 M NaCl solution revealed that the layer of silane doped with Ce was more protective than that of the non-modified one. It has been determined that the presence of cerium nitrate in the silane coating can lead to high values of low frequency impedance due to the healing of the defect.

引用

页码：127 / 135

页数：9

共 33 条

[1] THE INVESTIGATION OF CERIUM AS A CATHODIC INHIBITOR FOR ALUMINUM-COPPER ALLOYS [J].

ALDYKIEWICZ, AJ ;

ISAACS, HS ;

DAVENPORT, AJ .

JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1995, 142 (10) :3342-3350

[2] Surface characterisation of cerium layers on galvanised steel [J].

Arenas, MA ;

de Damborenea, JJ .

SURFACE & COATINGS TECHNOLOGY, 2004, 187 (2-3) :320-325

[3] Cerium-permanganate conversion coatings for a Zn-Co alloy [J].

Bikulcius, G. ;

Rucinskiene, A. ;

Sudavicius, A. ;

Burokas, V. ;

Griguceviciene, A. .

SURFACE & COATINGS TECHNOLOGY, 2008, 203 (1-2) :115-120

[4] A LINEAR KRONIG-KRAMERS TRANSFORM TEST FOR IMMITTANCE DATA VALIDATION [J].

BOUKAMP, BA .

JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1995, 142 (06) :1885-1894

[5] Active corrosion protection in Ce-modified hydrotalcite conversion coatings [J].

Buchheit, RG ;

Mamidipally, SB ;

Schmutz, P ;

Guan, H .

CORROSION, 2002, 58 (01) :3-14

[6] Analytical characterisation and corrosion behaviour of bis-[triethoxysilylpropyl]tetrasulphide pre-treated AA2024-T3 [J].

Cabral, A ;

Duarte, RG ;

Montemor, MF ;

Zheludkevich, ML ;

Ferreira, MGS .

CORROSION SCIENCE, 2005, 47 (03) :869-881

[7] Conversion-coating treatment for magnesium alloys by a permanganate-phosphate solution [J].

Chong, KZ ;

Shih, TS .

MATERIALS CHEMISTRY AND PHYSICS, 2003, 80 (01) :191-200

[8] REVIEW - REPLACEMENTS FOR CHROMIUM PRETREATMENTS ON ALUMINUM [J].

COHEN, SM .

CORROSION, 1995, 51 (01) :71-78

[9] Effects of inorganic additions on the performance of manganese-based conversion treatments [J].

Danilidis, I. ;

Hunter, J. ;

Scamans, G. M. ;

Sykes, J. M. .

CORROSION SCIENCE, 2007, 49 (03) :1559-1569

[10] Electrochemical investigation of the inhibition effect of CeO2 nanoparticles on the corrosion of mild steel [J].

Fedel, M. ;

Ahniyaz, A. ;

Ecco, L. G. ;

Deflorian, F. .

ELECTROCHIMICA ACTA, 2014, 131 :71-78

← 1 2 3 4 →