Study of the coating stability of a TBC system

被引：12
|
作者：
Guerre, C [1 ]
Molins, R [1 ]
Remy, L [1 ]
机构：
[1] ENSMP, Ctr Mat, CNRS, UMR 7633, F-91003 Evry, France
来源：
MATERIALS AT HIGH TEMPERATURES | 2000年 / 17卷 / 02期
关键词：
alumina scale; TBC; nickel aluminide; TEM; scale adhesion;
D O I：
10.3184/096034000783640848
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The degradation of thermal barrier coatings is closely linked to their spalling resistance which depends on the stability of the protective oxide scale produced by oxidation of the bond-coat. This study deals with a characterisation of the oxide layer, its interfaces with the bond-coat and the ceramic and their evolution during isothermal oxidation at 1,100 degrees C. The microstructural evolution of the bond-coat, the outer part of the superalloy and the ceramic layer was also studied.
引用
收藏
页码：197 / 203
页数：7
相关论文
共 50 条
  • [21] Different Growth Mechanisms of Alumina on the Surface of NiPtAl and MCrAlY Bondcoatings in EB-PVD TBC System
    Song Peng
    Lu Jiansheng
    Huang Taihong
    Zhang Defeng
    Lu Jianguo
    RARE METAL MATERIALS AND ENGINEERING, 2014, 43 (03) : 601 - 604
  • [22] High temperature interaction of volcanic ashes with 7YSZ TBC's produced by APS: Infiltration behavior and phase stability
    Rivera-Gil, Marco A.
    Gomez-Chavez, Juan J.
    Ramana, C., V
    Naraparaju, Ravisankar
    Schulz, Uwe
    Munoz-Saldana, Juan
    SURFACE & COATINGS TECHNOLOGY, 2019, 378
  • [23] Thermal stability of CrAlSiN coating by cathodic arc deposition with rotating cathodes
    Ho, Wei-Yu
    Chen, Chi-Wei
    Chang, Chi-Lung
    Wang, Da-Yung
    Ho, Woei-Yun
    ADVANCES IN HETEROGENEOUS MATERIAL MECHANICS 2008, 2008, : 496 - 500
  • [24] Parametric study for optimal design of an air plasma sprayed thermal barrier coating system with respect to thermal stress
    Lim, Jang Gyun
    Seo, Sangjae
    Koo, Jae Mean
    Seok, Chang Sung
    Choi, Jae Boong
    Kim, Moon Ki
    SURFACE & COATINGS TECHNOLOGY, 2017, 315 : 105 - 111
  • [25] Degradation process of Gd2Zr2O7 TBC system during static oxidation test
    Moskal, Grzegorz
    OCHRONA PRZED KOROZJA, 2011, 54 (4-5): : 186 - 191
  • [26] Prediction of Thermal Growth Stress in Thermal Barrier Coating System
    Wang Fenghui
    Wang Yongjun
    Wu Yingxi
    RARE METAL MATERIALS AND ENGINEERING, 2010, 39 (12) : 2122 - 2126
  • [27] Characterization of TBC systems with NiPtAl or NiCoCrAlYTa bond coatings after thermal cycling at 1100°C: a comparative study of failure mechanisms
    Put, Aurelie Vande
    Oquab, Djar
    Monceau, Daniel
    HIGH TEMPERATURE CORROSION AND PROTECTION OF MATERIALS 7, PTS 1 AND 2, 2008, 595-598 : 213 - 221
  • [28] Oxidation behaviour of a plasma-sprayed thermal barrier coating system
    Chen, WR
    Wu, X
    Patnaik, PC
    Immarigeon, JP
    SURFACE ENGINEERING: COATING AND HEAT TREATMENTS, PROCEEDINGS, 2003, : 535 - 543
  • [29] Study on behavior of NiAl coating with different Ni/Al ratios
    Wu, Qiong
    Li, Shusuo
    Ma, Yue
    Gong, Shengkai
    VACUUM, 2013, 93 : 37 - 44
  • [30] Study of Coating Effect on TEM Sample Damage and Elemental Analysis
    Xu, Yun
    Zhang, Fan
    Chen, Fairy
    CONFERENCE OF SCIENCE & TECHNOLOGY FOR INTEGRATED CIRCUITS, 2024 CSTIC, 2024,
12345