Kinetics of fluoride ion release from dental restorative glass ionomer cements: the influence of ultrasound, radiant heat and glass composition

To compare the effect of ultrasonic setting with self curing on fluoride release from conventional and experimental dental glass ionomer cements. To compare hand mixed and capsule mixing and the effect of replacing some of the reactive glass with zirconia. In a novel material which advocated using radiant heat to cure it, to compare the effect of this with ultrasound. To evaluate the effect of ultrasound on a glass ionomer with fluoride in the water but not in the glass. 10 samples of each cement were ultrasonically set for 55 s; 10 controls self cured for 6 min. Each was placed in 10 ml of deionised water which was changed at 1, 3, 7, 14, 21, 28 days. The solution fluoride content was measured using a selective ion electrode. All ultrasound samples released more fluoride than the controls. Release patterns were similar; after a few days, cumulative fluoride was linear with respect to t(1/2). Slope and intercept of linear regression plots increased with ultrasound. With radiant heat the cement released less fluoride than controls. The effect of ultrasound on cement with F in water increased only slope not intercept. Zirconia addition enhances fluoride release although the cement fluorine content is reduced. Comparison of capsule and hand mixing showed no consistent effect on fluoride release. Ultrasound enhances fluoride release from GICs. As heat has an opposite effect the heat from ultrasound is not its only action. The lesser effect on cement with fluoride only in the water indicates that of ultrasound enhances fluoride release from glass.