MECHANICAL CHARACTERIZATION OF THE ITER MOCK-UP INSULATION AFTER REACTOR IRRADIATION

The ITER mock-up project was launched in order to demonstrate the feasibility of an industrial impregnation process using the new cyanate ester / epoxy blend. The mock-up simulates the TF winding pack cross section by a stainless steel structure with the same dimensions as the TF winding pack at a length of I m. It consists of 7 plates simulating the double pancakes, each of them is wrapped with glass fiber / Kapton sandwich tapes. After stacking the 7 plates, additional insulation layers are wrapped to simulate the ground insulation This paper presents the results of the mechanical quality tests on the mock-up pancake insulation. Tensile and short beam shear specimens were cut from the plates extracted from the mock-up and tested at 77 K using a servo-hydraulic material testing device. All tests were repeated after reactor Irradiation to a fast neutron fluence of 1x10(22) m(-2) (E>0.1 MeV). In order to simulate the pulsed operation of ITER, tension-tension fatigue measurements were performed in the load controlled mode. Initial results show a high mechanical strength as expected from the high number of thin glass fiber layers, and an excellent homogeneity of the material.