PREPARATION OF TITANIUM CARBIDE POWDER FROM ILMENITE CONCENTRATE

被引：5

作者：

Gou, Hai-Peng ^{[1
,2
]}

Zhang, Guo-Hua ^{[1
]}

Chou, Kuo-Chih ^{[1
,2
]}

机构：

[1] Univ Sci & Technol Beijing, State Key Lab Adv Met, Beijing 100083, Peoples R China

[2] Univ Sci & Technol Beijing, Collaborat Innovat Ctr Universal Iron & Steel Tec, Beijing, Peoples R China

来源：

CHEMICAL INDUSTRY & CHEMICAL ENGINEERING QUARTERLY | 2017年 / 23卷 / 01期

基金：

中国国家自然科学基金;

关键词：

titanium carbide; ferric chloride solution; ilmenite concentrate; beta-FeOOH; CARBOTHERMIC REDUCTION; TIC NANOCOMPOSITE; BETA-FEOOH; AKAGANEITE; COMPOSITE; MECHANISMS; CARBON; FETIO3; TIO2;

D O I：

10.2298/CICEQ150521007G

中图分类号：

O69 [应用化学];

学科分类号：

081704 ;

摘要：

A new process of producing titanium carbide powder from ilmenite concentrate was put forward. The ilmenite concentrate was reduced by graphite powder at 1500 degrees C for 6 h, with the reduction products of TiC, Fe and MgO. The porous reduction products were agitation leached in ferric chloride solution at 25 degrees C for 60 min. After the filtration, TiC powder accompanied by little MgAl2O4 and Mg2SiO4 were obtained. Finally, the element Fe was recycled from the filtrate in the form of beta-FeOOH after blowing air for 3 hours at 80 degrees C. The size of rod-like, beta-FeOOH particle was less than 1 mu m.

引用

页码：67 / 72

页数：6

共 23 条

[1] GROWTH MECHANISMS OF IRON-OXIDE PARTICLES OF DIFFERING MORPHOLOGIES FROM THE FORCED HYDROLYSIS OF FERRIC-CHLORIDE SOLUTIONS
BAILEY, JK
BRINKER, CJ
MECARTNEY, ML
[J]. JOURNAL OF COLLOID AND INTERFACE SCIENCE, 1993, 157 (01) : 1 - 13
[2] Optimized standard state and solution properties of minerals .1. Model calibration for olivine, orthpyroxene, cordierite, garnet, ilmenite in the system FEO-MGO-CaO-Al2O3-TiO3-SiO2
Berman, RG
Aranovich, LY
[J]. CONTRIBUTIONS TO MINERALOGY AND PETROLOGY, 1996, 126 (1-2) : 1 - 24
[3] Rapid synthesis of TiC-Fe3C composite by electric discharge assisted mechanical milling of ilmenite (FeTiO3) with graphite
Calka, A.
Oleszak, D.
Stanford, N.
[J]. JOURNAL OF ALLOYS AND COMPOUNDS, 2008, 459 (1-2) : 498 - 500
[4] Ball milling assisted low temperature formation of iron-TiC composite
Chen, Y
[J]. SCRIPTA MATERIALIA, 1997, 36 (09) : 989 - 993
[5] SIMULTANEOUS REDUCTION AND CARBURIZATION OF ILMENITE
COLEY, KS
TERRY, BS
GRIEVESON, P
[J]. METALLURGICAL AND MATERIALS TRANSACTIONS B-PROCESS METALLURGY AND MATERIALS PROCESSING SCIENCE, 1995, 26 (03): : 485 - 494
[6] Akaganeite-type β-FeO(OH) nanocrystals:: preparation and characterization
Deliyanni, EA
Bakoyannakis, DN
Zouboulis, AI
Matis, KA
Nalbandian, L
[J]. MICROPOROUS AND MESOPOROUS MATERIALS, 2001, 42 (01) : 49 - 57
[7] Titanium carbide based composites for high temperature applications
Durlu, N
[J]. JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 1999, 19 (13-14) : 2415 - 2419
[8] Gou H. P., 2014, METALL MATER TRANS B, V46, P48
[9] THE INFLUENCE OF WEATHERING ON THE REDUCTION OF ILMENITE WITH CARBON
GUPTA, SK
RAJAKUMAR, V
GRIEVESON, P
[J]. METALLURGICAL TRANSACTIONS B-PROCESS METALLURGY, 1989, 20 (05): : 735 - 745
[10] PLASTIC BEHAVIOR OF TITANIUM CARBIDE
HOLLOX, GE
SMALLMAN, RE
[J]. JOURNAL OF APPLIED PHYSICS, 1966, 37 (02) : 818 - &

← 1 2 3 →