Mechanomaking of high speed steel AISI M2 powders fabrication

被引：5

作者：

Matteazzi, P ^{[1
]}

Wolf, F ^{[1
]}

机构：

[1] Univ Udine, Dipartimento Sci & Tecnol Chim, I-33100 Udine, Italy

来源：

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING | 1998年 / 246卷 / 1-2期

关键词：

nanophase materials; high speed steels; powder metallurgy; Mossbauer spectroscopy;

D O I：

10.1016/S0921-5093(97)00748-X

中图分类号：

TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

High speed steel AISI M2 was obtained by high energy milling from the elemental powders. The kinetics of synthesis were followed by Mossbauer spectroscopy and X-ray diffraction. About 14 h are required to complete alloying (12 at.% solute content) of the matrix and formation of carbides (M6C and Fe3C) all having grain sizes below 20 nm. The mean particle size was 50 mu m and the individual particles were almost fully dense. Limited grain growth to < 100 nm at temperatures up to 1300 degrees C was observed. This new concept for the fabrication of alloys and materials is suggested to be termed mechanomaking. (C) 1998 Elsevier Science S.A. All rights reserved.

引用

页码：235 / 243

页数：9

共 50 条

[21] Transverse rupture strenght of M3:2 high speed steel produced through conventional casting and powder metallurgy techniques
Araujo Filho, Oscar O.
Liberati, Joao F.
Monteiro, Waldemar Alfredo
Neves, Mauricio D.
Elias Da Silva, Luis C.
Ambrozio Filho, Francisco
ADVANCED MATERIALS FORUM III, PTS 1 AND 2, 2006, 514-516 : 584 - 588
[22] EFFECT OF HEAT TREATMENT PROCESS OF SINTERED M3/2 HIGH SPEED STEEL PARTS
Manaf, Samsiah Abdul
Selamat, Mohd Asri
Jaafar, Talib Ria
Mahaidin, Ahmad Aswad
ADVANCED MATERIALS CONFERENCE (AMC 2012), 2014, 879 : 180 - 183
[23] High Performance in EDM Machining of AISI D2 Hardened Steel
Hamid, Faizul Ezmat Abdul
Lajis, Mohd Amri
ADVANCES IN MATERIALS PROCESSING X, 2012, 500 : 259 - 265
[24] Direct fabrication of high-performance high speed steel products enhanced by LaB6
Zhang Qiankun
Jiang Yao
Shen Weijun
Zhang Huibin
He Yuehui
Lin Nan
Liu, C. T.
Huang Han
Huang Xiaolin
MATERIALS & DESIGN, 2016, 112 : 469 - 478
[25] Effect of Boride Layer on PM HSS AISI M2 on the Mechanisms Acting in the Transverse Rupture Strength Test
Arcego, Mateus Leal
Milan, Julio Cesar Giubilei
da Costa, Cesar Edil
dos Santos de Almeida, Elisangela Aparecida
MATERIALS RESEARCH-IBERO-AMERICAN JOURNAL OF MATERIALS, 2018, 21 (01):
[26] PROCESSING OF AISI M2 HSS WITH ADDITION OF NbC BY MECHANICAL ALLOYING USING TWO DIFFERENT TYPES OF ATTRITOR MILLS
de Araujo Filho, Oscar Olimpio
Martins das Neves, Mauricio David
Gonzalez, Cezar Henrique
Urtiga Filho, Severino Leopoldino
Ambrozio Filho, Francisco
ADVANCED POWDER TECHNOLOGY VII, 2010, 660-661 : 17 - 22
[27] Mechanical properties of composite materials consisting of M3/2 high speed steel reinforced with niobium carbides
Jimenez, J. A.
Frommeyer, G.
Lopez, M.
Candela, N.
Ruano, O. A.
THERMEC 2006, PTS 1-5, 2007, 539-543 : 756 - +
[28] Improved the microstructures and properties of M3:2 high-speed steel by spray forming and niobium alloying
Lu, L.
Hou, L. G.
Zhang, J. X.
Wang, H. B.
Cui, H.
Huang, J. F.
Zhang, Y. A.
Zhang, J. S.
MATERIALS CHARACTERIZATION, 2016, 117 : 1 - 8
[29] Friction and wear of lubricated M3 Class 2 sintered high speed steel with and without TiC and MnS additives
Zalisz, Z
Watts, A
Mitchell, SC
Wronski, AS
WEAR, 2005, 258 (5-6) : 701 - 711
[30] Mechanical and microstructural characterisation of P/M high-speed steel valve seat inserts
Santos, JC
Colosio, MA
ADVANCED POWDER TECHNOLOGY III, 2003, 416-4 : 312 - 316

← 1 2 3 4 5 →