Study of hourglass-shaped specimens for the analysis of compression behaviour in fibre direction of FRP composites using compression and four-point bending tests

被引：6
作者：
Cocchi, A. [1 ]
Montagnier, O. [2 ]
Hochard, C. [1 ]
机构：
[1] Aix Marseille Univ, CNRS, UMR 7031, Cent Marseille,LMA, 4 Impasse Nikola Tesla, F-13453 Marseille 13, France
[2] Ecole Air, Ctr Rech, CReA, BA 701, F-13661 Salon Air, France
来源：
COMPOSITES PART A-APPLIED SCIENCE AND MANUFACTURING | 2021年 / 144卷
关键词：
Glass fibres; Failure; Mechanical testing; Finite element analysis (FEA); STRENGTH; FAILURE; TENSILE; 3-POINT; REDUCTION; MODULUS; STRAIN; SIZE;
D O I：
10.1016/j.compositesa.2021.106332
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Flat hourglass specimens are proposed to assess the compressive behaviour of FRP utilizing two testing techniques. The hourglass shape helped to ensure failure at the centre of the specimen and to minimize in -plane stress concentration in this zone. Four-point bending tests are carried out and measures are performed via DIC. A procedure to calculate bending moment is proposed and validated in presence of large displacements. To evaluate the specimen and the method proposed, two different materials were tested, an E-glass/Epoxy unbalanced woven and a Carbon/PEEK balanced woven. In a second time ASTM D695 compression tests are carried out on the E-Glass/Epoxy composite to compare the hourglass specimens to the standardized dog-bone. The two testing techniques are analysed and compared.
引用
收藏
页数：12
相关论文
共 31 条
[1]   MODELING AND IDENTIFICATION OF THE MECHANICAL-BEHAVIOR OF COMPOSITE LAMINATES IN COMPRESSION [J].
ALLIX, O ;
LADEVEZE, P ;
VITTECOQ, E .
COMPOSITES SCIENCE AND TECHNOLOGY, 1994, 51 (01) :35-42
[2]  
[Anonymous], 1996, ANN BOOK ASTM, P78
[3]   Effect of sea water and humidity on the tensile and compressive properties of carbon-polyamide 6 laminates [J].
Arhant, Mael ;
Le Gac, Pierre-Yves ;
Le Gall, Maelenn ;
Burtin, Christian ;
Briancon, Christophe ;
Davies, Peter .
COMPOSITES PART A-APPLIED SCIENCE AND MANUFACTURING, 2016, 91 :250-261
[4]   EVALUATION OF THE IITRI COMPRESSION TEST METHOD FOR STIFFNESS AND STRENGTH DETERMINATION [J].
BOGETTI, TA ;
GILLESPIE, JW ;
PIPES, RB .
COMPOSITES SCIENCE AND TECHNOLOGY, 1988, 32 (01) :57-76
[5]   On the tension-tension fatigue behaviour of a carbon reinforced thermoplastic part II: Evaluation of a dumbbell-shaped specimen [J].
De Baere, I. ;
Van Paepegem, W. ;
Hochard, C. ;
Degrieck, J. .
POLYMER TESTING, 2011, 30 (06) :663-672
[6]   Design of a composite tube to analyze the compressive behavior of CFRP [J].
Eyer, G. ;
Montagnier, O. ;
Charles, J. -P. ;
Hochard, C. .
COMPOSITES PART A-APPLIED SCIENCE AND MANUFACTURING, 2016, 87 :115-122
[7]  
Eyer G, 2015, THESIS AIX MARSEILLE
[8]  
Eyer G, 2013, COMPTES RENDUS JNC 1, V13, P11
[9]   Simplified compression bending test method for advanced composites [J].
Fukuda, H ;
Itabashi, M .
COMPOSITES PART A-APPLIED SCIENCE AND MANUFACTURING, 1999, 30 (03) :249-256
[10]   PROBLEMS ASSOCIATED WITH THE COMPRESSION TESTING OF FIBER REINFORCED PLASTIC COMPOSITES [J].
HARPER, JF ;
MILLER, NA ;
YAP, SC .
POLYMER TESTING, 1993, 12 (01) :15-29
1234