Role of detonation gun spray Cr3C2-NiCr coating in improving high temperature corrosion resistance of SAE-213-T22 and SAE-347H steel in presence of Na2SO4-82%Fe2(SO4)3 salt deposits

被引：38
作者：
Kaur, M. [2 ]
Singh, H. [1 ]
Prakash, S. [3 ]
机构：
[1] Indian Inst Technol, Roopnagar, India
[2] Baba Banda Singh Bahadur Engn Coll, Fatehgarh Sahib, India
[3] India Inst Technol, Roorkee, Uttar Pradesh, India
来源：
SURFACE ENGINEERING | 2010年 / 26卷 / 06期
关键词：
Coatings; D-gun spray coatings; Cr3C2-NiCr; High temperature corrosion; Molten salt environment; Oxide scale; HOT CORROSION; EROSION-CORROSION; WEAR BEHAVIOR; WC-CO; HVOF; NI; ENVIRONMENT; OXIDATION; VELOCITY; PLASMA;
D O I：
10.1179/026708409X12490360425963
中图分类号：
TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
Cr3C2-NiCr coatings were sprayed on SAE-213-T22 and SAE-347H boiler steels by detonation gun spray process. High temperature corrosion studies were conducted on the uncoated as well as detonation gun sprayed specimens in a molten salt environment at 700 degrees C under cyclic conditions. The molten salt comprising Na2SO4-82% Fe-2(SO4)(3) was applied on the specimens as a deposit. The weight change technique was used to establish kinetics of the corrosion. X-ray diffraction, field emission scanning electron microscopy/energy dispersive spectroscopy and X-ray mapping techniques were used to analyse the corrosion products. SAE-213-T22 steel suffered an accelerated corrosion in the form of intense spalling of its oxide scale, whereas SAE-347H steel exhibited only marginal spallation in the form of fine powder. The Cr3C2-NiCr coating showed good adherence to the boiler steels during the exposure with no tendency for spallation of its oxide scale. The coating was found to be successful in developing resistance against hot corrosion in the molten salt environment, which may be attributed to the formation of oxides of nickel and chromium.
引用
收藏
页码：428 / 439
页数：12
相关论文
共 48 条
[1]  
BLATCHFORD MT, 2001, THERMAL SPRAY 2001 N
[2]  
Brasunas A. S., 1977, NACE BASIC CORROSION, P1
[3]   Processing and properties of a 85%Cr3C2-10.5%Ni-4.5%Fe cermet [J].
Eroglu, S ;
Duran, C .
SCRIPTA MATERIALIA, 1997, 37 (07) :991-997
[4]  
Fukuda Y., 1988, P INT S ADV THERM SP, P49
[5]  
GOWARD GW, 1986, MATER SCI TECH SER, V2, P194, DOI 10.1179/026708386790123314
[6]   Oxidation of Inconel 718 in air at high temperatures [J].
Greene, GA ;
Finfrock, CC .
OXIDATION OF METALS, 2001, 55 (5-6) :505-521
[7]   Comparative study of Cr3C2-NiCr coatings obtained by HVOF and hard chromium coatings [J].
Guilemany, J. M. ;
Espallargas, N. ;
Suegama, P. H. ;
Benedetti, A. V. .
CORROSION SCIENCE, 2006, 48 (10) :2998-3013
[8]  
Guilemany JM, 1998, SURFACE MODIFICATION TECHNOLOGIES XI, P81
[9]   Thermal barrier coatings for enhanced efficiency of gas turbine engines [J].
Gurrappa, I. ;
Rao, A. Sambasiva .
SURFACE & COATINGS TECHNOLOGY, 2006, 201 (06) :3016-3029
[10]   Synthesis of nanostructured Cr3C2-25(Ni20Cr) coatings [J].
He, JH ;
Ice, M ;
Lavernia, EJ .
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2000, 31 (02) :555-564
12345