Mechanical properties of BPDA-ODA polyimide fibers

被引:76
作者
Zhang, QH [1 ]
Dai, M
Ding, MX
Chen, D
Gao, LX
机构
[1] Donghua Univ, Coll Mat Sci & Engn, State Key Lab Chem Fibers & Polymer Mat, Shanghai 200051, Peoples R China
[2] Chinese Acad Sci, Changchun Inst Appl Chem, State Key Lab Polymer Phys & Chem, Changchun 130022, Peoples R China
基金
中国国家自然科学基金;
关键词
polyimide; high performance fibers; mechanical properties;
D O I
10.1016/j.eurpolymj.2004.06.020
中图分类号
O63 [高分子化学(高聚物)];
学科分类号
070305 ; 080501 ; 081704 ;
摘要
An aromatic polyimide was synthesized via a one-step polycondensation reaction between biphenyltetracarboxylic dianhydride (BPDA) and 4,4'-oxydianiline (ODA) in p-chlorophenol. The polyimide (BPDA-ODA) solution dopes were spun into fibers by means of dry-jet wet spinning. The as-spun fibers were drawn and treated in heating tubes for improving the mechanical properties. The thermal treatment on the fibers resulted in a relatively high tensile strength and modulus. Thermal mechanical analysis (TMA) was employed to study the linear coefficient of thermal expansion (CTE). Thermal gravimetry analysis (TGA) spectra showed that the BPDA-ODA fibers possessed an excellent property of thermo-oxidative degradation resistance. The sonic modulus E-s of the polyimide fibers was measured. (C) 2004 Elsevier Ltd. All rights reserved.
引用
收藏
页码:2487 / 2493
页数:7
相关论文
共 30 条
[1]   HIGH-MODULUS HIGH-STRENGTH POLY-(PARA-PHENYLENE BENZOBISTHIAZOLE) FIBERS .1. HEAT-TREATMENT PROCESSING [J].
ALLEN, SR ;
FARRIS, RJ ;
THOMAS, EL .
JOURNAL OF MATERIALS SCIENCE, 1985, 20 (08) :2727-2734
[2]  
[Anonymous], TEXT RES J
[3]   Characterisation of poly(p-phenylenebenzobisoxazole) fibres by solid state NMR [J].
Bourbigot, S ;
Flambard, X ;
Revel, B .
EUROPEAN POLYMER JOURNAL, 2002, 38 (08) :1645-1651
[4]   A HIGH-PERFORMANCE AROMATIC POLYIMIDE FIBER .1. STRUCTURE, PROPERTIES AND MECHANICAL-HISTORY DEPENDENCE [J].
CHENG, SZD ;
WU, ZQ ;
EASHOO, M ;
HSU, SLC ;
HARRIS, FW .
POLYMER, 1991, 32 (10) :1803-1810
[5]   WET SPINNING OF SOLID POLYAMIC ACID FIBERS [J].
DOROGY, WE ;
STCLAIR, AK .
JOURNAL OF APPLIED POLYMER SCIENCE, 1991, 43 (03) :501-519
[6]   FIBERS FROM A SOLUBLE, FLUORINATED POLYIMIDE [J].
DOROGY, WE ;
STCLAIR, AK .
JOURNAL OF APPLIED POLYMER SCIENCE, 1993, 49 (03) :501-510
[7]   HIGH-PERFORMANCE AROMATIC POLYIMIDE FIBERS .3. A POLYIMIDE SYNTHESIZED FROM 3,3',4,4'-BIPHENYLTETRACARBOXYLIC DIANHYDRIDE AND 2,2'-DIMETHYL-4,4'-DIAMINOBIPHENYL [J].
EASHOO, M ;
WU, ZQ ;
ZHANG, AQ ;
SHEN, DX ;
TSE, C ;
HARRIS, FW ;
CHENG, SZD ;
GARDNER, KH ;
HSIAO, BS .
MACROMOLECULAR CHEMISTRY AND PHYSICS, 1994, 195 (06) :2207-2225
[8]  
Edwards WM, 1965, Patent No. [3179614A, 3179614]
[9]   ARTICULATED ALL-PARA POLYMERS WITH 2,6-BENZOBISOXAZOLE, 2,6-BENZOBISTHIAZOLE, AND 2,6-BENZOBISIMIDAZOLE UNITS IN THE BACKBONE [J].
EVERS, RC ;
ARNOLD, FE ;
HELMINIAK, TE .
MACROMOLECULES, 1981, 14 (04) :925-930
[10]  
HILDAO CJ, 1974, REINFORCED PHENOLIC