Temperature dependence of high-cycle fatigue behavior of a Ni-base single crystal superalloy

被引：2
作者：
Liu, Y. [1 ,2 ]
Yu, J. J. [1 ]
Xu, Y. [1 ]
Sun, X. F. [1 ]
Guan, H. R. [1 ]
Hu, Z. Q. [1 ]
机构：
[1] Chinese Acad Sci, Inst Met Res, Shenyang 110016, Peoples R China
[2] Chinese Acad Sci, Grad Sch, Beijing 100039, Peoples R China
来源：
2006 BIMW: 2006 BEIJING INTERNATIONAL MATERIALS WEEK, PTS 1-4: MAGNESIUM | 2007年 / 546-549卷
关键词：
single crystal; high-cycle fatigue; secondary gamma' phase; microstructure;
D O I：
10.4028/www.scientific.net/MSF.546-549.1219
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Smooth specimens of single crystal (SC) superalloy SRR99 with [001] orientation were subjected to high-cycle fatigue (HCF) loading at temperatures of 700 degrees C, 760 degrees C, 850 degrees C and 900 degrees C in air atmosphere. The results demonstrated that conditional fatigue strength reached the maximum at 760 degrees C and decreases with increasing temperature. Analysis on fracture surface showed a trend for cleavage rupture at 850 degrees C and 900 degrees C and ductile rupture at 700 degrees C and 760 degrees C. Fatigue cracks initiated at the surface or subsurface were primarily responsible for the ultimate failure. The influence of testing temperature on fatigue lifetime was studied by examining evolution of the microstructure through SEM observation. With the process of cyclic loading at elevated temperatures, the primary cuboidal gamma' precipitates tended to agglomerate and spheroidized, meanwhile a larger number of secondary gamma' particles were formed in the gamma matrix in specimens fatigue tested at 700 degrees C, which would have a significant effect on the high temperature properties.
引用
收藏
页码：1219 / +
页数：2
相关论文
共 50 条
  • [21] Effect of microstructure on thermo-mechanical and isothermal low cycle fatigue failures of a single crystal Ni-base superalloy
    Sakaguchi, Motoki
    Okazaki, Masakazu
    [J]. PROGRESSES IN FRACTURE AND STRENGTH OF MATERIALS AND STRUCTURES, 1-4, 2007, 353-358 : 491 - 494
  • [22] Anisotropic Oxidation Resistance in a Ni-Base Single Crystal Superalloy
    Latief, Fahamsyah H.
    Alrasheedi, Nashmi H.
    [J]. INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE, 2015, 10 (03): : 2183 - 2193
  • [23] Effect of skew angle of holes on the tensile behavior of a Ni-base single crystal superalloy
    Zhou, Z. J.
    Wang, L.
    Wen, J. L.
    Lou, L. H.
    Zhang, J.
    [J]. JOURNAL OF ALLOYS AND COMPOUNDS, 2015, 628 : 158 - 163
  • [24] Stress-induced formation of TCP phases during high temperature low cycle fatigue loading of the single-crystal Ni-base superalloy ERBO/1
    Meid, Carla
    Eggeler, Mario
    Watermeyer, Philipp
    Kostka, Aleksander
    Hammerschmidt, Thomas
    Drautz, Ralf
    Eggeler, Gunther
    Bartsch, Marion
    [J]. ACTA MATERIALIA, 2019, 168 : 343 - 352
  • [25] Very high cycle fatigue of a notched Ni-based single crystal superalloy at high temperature
    Morales, A. Vicente
    Mauget, F.
    Larrouy, B.
    Villechaise, P.
    Cormier, J.
    [J]. INTERNATIONAL JOURNAL OF FATIGUE, 2024, 186
  • [26] Effect of high temperature air-exposure on room temperature fatigue crack growth of Ni-base single crystal superalloy CMSX-10
    Lino, Y
    [J]. ADVANCES IN FRACTURE AND FAILURE PREVENTION, PTS 1 AND 2, 2004, 261-263 : 1191 - 1196
  • [27] Effect of Shaped Film Cooling Hole Manufacturing Defects on the High-Cycle Fatigue Behavior of a Ni-Based Single-Crystal Superalloy
    Wang, Yue
    Jiang, Rong
    Chen, Mo
    Li, Xiaoyu
    Lu, Xuping
    Zha, Haiyong
    Song, Yingdong
    [J]. FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2025,
  • [28] Crystal plasticity analysis of cylindrical indentation on a Ni-base single crystal superalloy
    Sabnis, Prajwal A.
    Forest, Samuel
    Arakere, Nagaraj K.
    Yastrebov, Vladislav A.
    [J]. INTERNATIONAL JOURNAL OF PLASTICITY, 2013, 51 : 200 - 217
  • [29] On the stress and temperature dependence of low temperature and high stress shear creep in Ni-base single crystal superalloys
    Burger, D.
    Dlouhy, A.
    Yoshimi, K.
    Eggeler, G.
    [J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2020, 795
  • [30] The Influence of Dwell Time on Low Cycle Fatigue Behavior of Ni-base Superalloy IC10
    Wang, Anqiang
    Liu, Lu
    Wen, Zhixun
    Li, Zhenwei
    Yue, Zhufeng
    [J]. HIGH TEMPERATURE MATERIALS AND PROCESSES, 2017, 36 (08) : 795 - 803
12345