Lifetime and failure modes of plasma sprayed thermal barrier coatings in thermal gradient rig tests with simultaneous CMAS injection

被引:49
作者
Mack, Daniel E. [1 ]
Wobst, Tanja [1 ,2 ]
Jarligo, Maria Ophelia D. [1 ,3 ]
Sebold, Doris [1 ]
Valssen, Robert [1 ]
机构
[1] Forschungszentrum Julich, Inst Energy & Climate Res, Mat Synth & Proc IEK 1, D-52425 Julich, Germany
[2] Rolls Royce Deutschland Ltd & Co KG, Eschenweg 11, D-15827 Blankenfelde Mahlow, Germany
[3] Quantiam Technol Inc, 1651 94 St NW, Edmonton, AB T6N 1E6, Canada
关键词
Thermal barrier coatings (TBCs); Atmospheric plasma spraying (APS); Gradient burner rig test; Calcium magnesium alumino-silicate (CMAS); Spallation lifetime; DAMAGE MECHANISMS; DELAMINATION; TEMPERATURE; DEGRADATION; SPALLATION; VISCOSITY; GLASS; CORROSION; DEPOSITS; CRACKING;
D O I
10.1016/j.surfcoat.2017.04.071
中图分类号
TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
Degradation of thermal barrier coatings (TBCs) in gas-turbine engines due to calcium-magnesium-aluminosilicate (CMAS) glassy deposits from various sources such as sand, volcanic ash, fly ash, or variable quality fuels has been a tenacious issue during the recent years. This follows from the fact that engines are required to operate under increasingly harsh conditions in all kind of gas turbine applications following the demands for higher efficiency and operational flexibility. While the understanding of the mechanism of CMAS induced degradation of TBCs as well as approaches for mitigation of CMAS attack by means of advanced TBC compositions have grown remarkably, most of the reported results have been obtained from lab testing at isothermal conditions or from evaluation of ex-service components, either. The isothermal tests are not reproducing important thermomechanical effects from service conditions, and it may be hard to figure out the thermal history of the ex-service examples. In this study a burner rig facility has been used for the evaluation of TBC performance, where a thermal gradient is applied across the TBC at cyclic load and CMAS is continuously injected to the combustion environment to simulate the conditions closer to actual service in an engine while allowing control of important degradation limiting parameters. Tests have been performed on the state of the art material YSZ while loading parameters as high temperature dwell time and CMAS deposition rate have been varied. Tests have been evaluated in terms of chemical degradation, failure mode and TBC spallation lifetime by means of SEM, EDS and XRD. Test conditions and relevance to in-service operating conditions are discussed. Major impacts on thermal gradient cycling lifetime and similarities and discrepancies related to reported failure mechanism are reviewed. (C) 2017 Published by Elsevier B.V.
引用
收藏
页码:36 / 47
页数:12
相关论文
共 46 条
[31]   TURBINE AIRFOIL DEGRADATION IN THE PERSIAN-GULF-WAR [J].
SMIALEK, JL ;
ARCHER, FA ;
GARLICK, RG .
JOM-JOURNAL OF THE MINERALS METALS & MATERIALS SOCIETY, 1994, 46 (12) :39-41
[32]  
Steinke T., 2011, INFLUENCE CMAS TACK, V276
[33]   A novel test approach for plasma-sprayed coatings tested simultaneously under CMAS and thermal gradient cycling conditions [J].
Steinke, Tanja ;
Sebold, Doris ;
Mack, Daniel E. ;
Vassen, Robert ;
Stoever, Detlev .
SURFACE & COATINGS TECHNOLOGY, 2010, 205 (07) :2287-2295
[34]   Damage mechanisms, life prediction, and development of EB-PVD thermal barrier coatings for turbine airfoils [J].
Strangman, Tom ;
Raybould, Derek ;
Jameel, Ahsan ;
Baker, Wil .
SURFACE & COATINGS TECHNOLOGY, 2007, 202 (4-7) :658-664
[35]   The Influence of Transient Thermal Gradients and Substrate Constraint on Delamination of Thermal Barrier Coatings [J].
Sundaram, S. ;
Lipkin, D. M. ;
Johnson, C. A. ;
Hutchinson, J. W. .
JOURNAL OF APPLIED MECHANICS-TRANSACTIONS OF THE ASME, 2013, 80 (01)
[36]   Thermal cycling setup for testing thermal barrier coatings [J].
Traeger, F ;
Vassen, R ;
Rauwald, KH ;
Stöver, D .
ADVANCED ENGINEERING MATERIALS, 2003, 5 (06) :429-+
[37]   Damage mechanisms and lifetime behavior of plasma sprayed thermal barrier coating systems for gas turbines - Part 1: Experiments [J].
Trunova, O. ;
Beck, T. ;
Herzog, R. ;
Steinbrech, R. W. ;
Singheiser, L. .
SURFACE & COATINGS TECHNOLOGY, 2008, 202 (20) :5027-5032
[38]   Viscosity predictions of the slag composition of gasified coal, utilizing FactSage equilibrium modelling [J].
van Dyk, J. C. ;
Waanders, F. B. ;
Benson, S. A. ;
Laumb, M. L. ;
Hack, K. .
FUEL, 2009, 88 (01) :67-74
[39]   CMAS corrosion of EB PVD TBCs: Identifying the minimum level to initiate damage [J].
Wellman, R. ;
Whitman, G. ;
Nicholls, J. R. .
INTERNATIONAL JOURNAL OF REFRACTORY METALS & HARD MATERIALS, 2010, 28 (01) :124-132
[40]   Erosion, corrosion and erosion-corrosion of EB PVD thermal barrier coatings [J].
Wellman, R. G. ;
Nicholls, J. R. .
TRIBOLOGY INTERNATIONAL, 2008, 41 (07) :657-662