Portland 3D Printing of Portland Cement Pastes with Additions of Kaolin, Superplastificant, and Calcium Carbonate

被引：0
|
作者：
Vergara, Luis A. [1 ]
Colorado, Henry A. [1 ,2 ]
机构：
[1] Univ Antioquia UdeA, CCComposites Lab, Calle 70 52-21, Medellin, Colombia
[2] Univ Antioquia, Fac Ingn, Bloque 20,Calle 67 53-108, Medellin, Colombia
来源：
TMS 2020 149TH ANNUAL MEETING & EXHIBITION SUPPLEMENTAL PROCEEDINGS | 2020年
关键词：
3D printing; Additive manufacturing; Portland cement; Mortar; Kaolin; direct ink writing; CONCRETE; PERFORMANCE; DESIGN;
D O I：
10.1007/978-3-030-36296-6_20
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The main goal in this investigation is to develop inexpensive formulations of Portland cement pastes for additive manufacturing using the direct ink writing technique. Kaolin, a superplastificant, and calcium carbonate additions were used as additives and modifiers of the printing material. A total of 3 formulations were developed with acceptable shape stability and finishing of the manufactured parts. Cylindrical samples of 17 mm in diameter and 26 mm of height were built in order to be tested in compression tests. The microstructure was characterized with scanning electron microscopy, density, and compression tests. Results showed one formulation to be the best one, which was associated mainly to an optimal kaolin content as rheology regulator.
引用
收藏
页码：217 / 226
页数：10
相关论文
共 50 条
  • [21] SATURATION FACTORS FOR CALCIUM HYDROXIDE AND CALCIUM SULFATES IN FRESH PORTLAND-CEMENT PASTES
    GARTNER, EM
    TANG, FJ
    WEISS, SJ
    JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1985, 68 (12) : 667 - 673
  • [22] Microtensile testing and 3D imaging of hydrated Portland cement
    Trtik, P.
    Staehli, P.
    Landis, E. N.
    Stampanoni, M.
    van Mier, J. G. M.
    FRACTURE MECHANICS OF CONCRETE AND CONCRETE STRUCTURES, VOLS 1-3: VOL 1: NEW TRENDS IN FRACTURE MECHANICS OF CONCRETE; VOL 2: DESIGN, ASSESSMENT AND RETROFITTING OF RC STRUCTURES; VOL 3: HIGH-PERFORMANCE CONCRETE, BRICK-MASONRY AND ENVIRONMENTAL ASPECTS, 2007, 1-3 : 1277 - +
  • [23] Properties of high calcium fly ash geopolymer pastes with Portland cement as an additive
    Phoo-ngernkham, Tanakorn
    Chindaprasirt, Prinya
    Sata, Vanchai
    Pangdaeng, Saengsuree
    Sinsiri, Theerawat
    INTERNATIONAL JOURNAL OF MINERALS METALLURGY AND MATERIALS, 2013, 20 (02) : 214 - 220
  • [24] Effects of calcium nitrate and triisopropanolamine on the setting and strength evolution of Portland cement pastes
    Chikh, N.
    Cheikh-Zouaoui, M.
    Aggoun, S.
    Duval, R.
    MATERIALS AND STRUCTURES, 2008, 41 (01) : 31 - 36
  • [25] A model for two types of calcium silicate hydrate in the microstructure of Portland cement pastes
    Tennis, PD
    Jennings, HM
    CEMENT AND CONCRETE RESEARCH, 2000, 30 (06) : 855 - 863
  • [26] Properties of high calcium fly ash geopolymer pastes with Portland cement as an additive
    Tanakorn Phoo-ngernkham
    Prinya Chindaprasirt
    Vanchai Sata
    Saengsuree Pangdaeng
    Theerawat Sinsiri
    International Journal of Minerals Metallurgy and Materials, 2013, 20 (02) : 214 - 220
  • [27] Properties of high calcium fly ash geopolymer pastes with Portland cement as an additive
    Tanakorn Phoo-ngernkham
    Prinya Chindaprasirt
    Vanchai Sata
    Saengsuree Pangdaeng
    Theerawat Sinsiri
    International Journal of Minerals, Metallurgy, and Materials, 2013, 20 : 214 - 220
  • [28] Effects of calcium nitrate and triisopropanolamine on the setting and strength evolution of Portland cement pastes
    N. Chikh
    M. Cheikh-Zouaoui
    S. Aggoun
    R. Duval
    Materials and Structures, 2008, 41 : 31 - 36
  • [29] MICROCRYSTALLINE CALCIUM HYDROXIDE IN PORTLAND-CEMENT PASTES OF LOW WATER-CEMENT RATIO
    GROVES, GW
    CEMENT AND CONCRETE RESEARCH, 1981, 11 (5-6) : 713 - 718
  • [30] 3D printing of ordinary Portland cement with waste wood derived biochar obtained from gasification
    Vergara, Luis A.
    Perez, Juan F.
    Colorado, Henry A.
    CASE STUDIES IN CONSTRUCTION MATERIALS, 2023, 18
12345