PLICATION OF X-RAY DIFFRACTION TO ANALYSE PHASE COMPOSITION OF ALUMINIUM ALLOYS FOR PLASTIC WORKING

An attempt was made to determine phase composition of commercial aluminium alloys using X-ray diffraction. Samples for phase composition analysis were selected from the group of aluminium alloys covered by the EN 573-3:2013 standard [1]. Representative samples were taken from eight groups of alloys with different chemical composition (at least one sample from each group). The diffraction intensity was measured with a standard X-ray diffractometer in Bragg-Brentano geometry in a way that allowed identification of the weakest diffraction peaks. As a results of the performed research it has been shown that X-ray phase analysis can be used to identify the matrix of aluminium alloys, Si and crystalline intermetallic phases such as Mg2Si, Al93.38Cu6.02Fe24Si16.27, Al4.01MnSi0.74, MgZn2, Al-17(Fe3.2Mn0.8) Si-2, Al65Cu20Fe15, and Cu3Mn2Al. The detectability limit of the above-mentioned phases is better than 0.5%. The research has also shown that X-ray phase analysis is applicable in the investigation of phase transformations taking place in aluminium alloys.