Shielding AC magnetic fields using commercial YBa2Cu3O7-coated conductor tapes

被引：24

作者：

Kvitkovic, J. ^{[1
]}

Pamidi, S. ^{[1
]}

Voccio, J. ^{[2
]}

机构：

[1] Florida State Univ, Ctr Adv Power Syst, Tallahassee, FL 32310 USA

[2] Amer Superconductor Corp, Devens, MA 01434 USA

来源：

SUPERCONDUCTOR SCIENCE & TECHNOLOGY | 2009年 / 22卷 / 12期

关键词：

D O I：

10.1088/0953-2048/22/12/125009

中图分类号：

O59 [应用物理学];

学科分类号：

摘要：

High temperature superconducting materials (HTS) offer several advantages in magnetic field shielding applications. HTS materials have the potential of creating efficient shields by reducing the size and weight of the shielding systems. The main limitation until recently has been the difficulty of producing HTS tapes of large width. Recent developments in second-generation (2G) high temperature YBCO superconductors allow the production of 2G films on very large 4 cm wide substrates. Magnetic field shielding properties of coils and sheets fabricated from 4 cm wide YBa2Cu3O7-coated conductors are reported. Shielding properties of shields with multiple layers were measured at liquid nitrogen temperatures. Magnetic field amplitude inside the superconducting shields was measured using Hall probes with a phase-sensitive technique. Efficacy of the shields was characterized at varying field amplitude and frequency. Shielding of up to 95% of applied magnetic field was observed at magnetic field amplitudes of <10 mT. The frequency dependence of shielding properties depended on the geometry of the shields.

引用

页数：7

共 6 条

[1] Field penetration into hard type-II superconducting tubes: effects of a cap, a non-superconducting joint, and non-uniform superconducting properties [J].

Denis, S. ;

Dirickx, M. ;

Vanderbemden, Ph ;

Ausloos, M. ;

Vanderheyden, B. .

SUPERCONDUCTOR SCIENCE & TECHNOLOGY, 2007, 20 (05) :418-427

[2] STUDY OF THE PROPAGATION OF AN AC MAGNETIC-FIELD THROUGH SUPERCONDUCTING THICK-FILMS [J].

KARTHIKEYAN, J ;

PAITHANKAR, AS ;

CHADDAH, P ;

SREEKUMAR, KP .

SUPERCONDUCTOR SCIENCE & TECHNOLOGY, 1991, 4 (06) :250-256

[3] Three-axis cryogenic Hall sensor [J].

Kvitkovic, J ;

Majoros, M .

JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS, 1996, 157 :440-441

[4] Progress in high temperature superconductor coated conductors and their applications [J].

Malozemoff, A. P. ;

Fleshler, S. ;

Rupich, M. ;

Thieme, C. ;

Li, X. ;

Zhang, W. ;

Otto, A. ;

Maguire, J. ;

Folts, D. ;

Yuan, J. ;

Kraemer, H-P ;

Schmidt, W. ;

Wohlfart, M. ;

Neumueller, H-W .

SUPERCONDUCTOR SCIENCE & TECHNOLOGY, 2008, 21 (03)

[5] MAGNETIC SHIELDING PROPERTIES OF HTC SUPERCONDUCTOR [J].

MATSUBA, H ;

YAHARA, A ;

IRISAWA, D .

SUPERCONDUCTOR SCIENCE & TECHNOLOGY, 1992, 5 :S432-S439

[6] Variable temperature total AC loss and stability characterization facility [J].

Pamidi, Sastry ;

Nguyen, Doan ;

Zhang, Guomin ;

Knoll, David ;

Trociewitz, Ulf ;

Schwartz, Justin .

IEEE TRANSACTIONS ON APPLIED SUPERCONDUCTIVITY, 2007, 17 (02) :3179-3182

← 1 →