Effect of Refractory on Nonmetallic Inclusions in Si-Mn-Killed Steel

被引:30
作者
Deng, Zhiyin [1 ,2 ,3 ]
Cheng, Liu [1 ,2 ,4 ]
Chen, Lei [1 ,2 ]
Zhu, Miaoyong [1 ,2 ]
机构
[1] Northeastern Univ, Minist Educ, Key Lab Ecol Met Multimetall Minerals, Shenyang 110819, Liaoning, Peoples R China
[2] Northeastern Univ, Sch Met, Shenyang 110819, Liaoning, Peoples R China
[3] Shandong Iron & Steel Cop Ltd, Laiwu Branch, Jinan 271104, Shandong, Peoples R China
[4] Northeastern Univ, Sch Mech Engn & Automat, Shenyang 110819, Liaoning, Peoples R China
基金
国家重点研发计划; 中国博士后科学基金;
关键词
alumina; inclusions; refractory; Si-Mn-killed steel; spinel; MEDIUM-MANGANESE STEEL; REACTION BEHAVIORS; SLAG; MECHANISM; MGO;
D O I
10.1002/srin.201900268
中图分类号
TF [冶金工业];
学科分类号
0806 ;
摘要
Some laboratory experiments are carried out to study the effect of different refractories on the original and exogenous inclusions in Si-Mn-killed steel. As expected, it is found that Al2O3 refractory causes high melting points of both SiO2-Al2O3-MnO system and SiO2-Al2O3-CaO system inclusions, while MgO crucible reduces the melting points of both systems of inclusions to a certain extent. The purity of MgO refractory is crucial for tire cord steel grades, and even 0.3% of Al2O3 impurity in refractory results in an evident increase (by 10%-20%) of Al2O3 content in the inclusions. Similar to Al-killed steel grades, MgO center dot Al2O3 spinel can also be stable in Si-Mn-killed steel due to the effect of MgO refractory, and MgO and Al2O3 inclusions can transform into MgO center dot Al2O3 spinel. These inclusions should be strictly controlled during refining process. High-purity and high-quality MgO refractory as well as high-quality alloys are recommended for Si-Mn-killed steel grades, and Al2O3-based refractory should be avoided.
引用
收藏
页数:12
相关论文
共 30 条
[1]   Three- Dimensional Investigations of Inclusions in Ferroalloys [J].
Bi, Yanyan ;
Karasev, Andrey ;
Jonsson, Par G. .
STEEL RESEARCH INTERNATIONAL, 2014, 85 (04) :659-669
[2]   A study on the mechanism of reaction between refractory materials and aluminium deoxidised molten steel [J].
Brabie, V .
STEEL RESEARCH, 1997, 68 (02) :54-60
[3]   Top slag refining for inclusion composition transform control in tire cord steel [J].
Chen, Shu-hao ;
Jiang, Min ;
He, Xiao-fei ;
Wang, Xin-hua .
INTERNATIONAL JOURNAL OF MINERALS METALLURGY AND MATERIALS, 2012, 19 (06) :490-498
[4]  
Chouda T, 2004, R D KOBE STEEL ENG R, V54, P25
[5]   Effect of Refractory on Nonmetallic Inclusions in Al-Killed Steel [J].
Deng, Zhiyin ;
Zhu, Miaoyong ;
Du Sichen .
METALLURGICAL AND MATERIALS TRANSACTIONS B-PROCESS METALLURGY AND MATERIALS PROCESSING SCIENCE, 2016, 47 (05) :3158-3167
[6]   Evolution Mechanism of Non-metallic Inclusions in Al-Killed Alloyed Steel during Secondary Refining Process [J].
Deng, Zhiyin ;
Zhu, Miaoyong .
ISIJ INTERNATIONAL, 2013, 53 (03) :450-458
[7]   Activities of the constituents in spinel solid solution and free energies of formation of MgO, MgO •Al2O3 [J].
Fujii, K ;
Nagasaka, T ;
Hino, M .
ISIJ INTERNATIONAL, 2000, 40 (11) :1059-1066
[8]   Experimental Determination of Mg Activities in Fe-Mg Solutions [J].
Gran, Jimmy ;
Du Sichen .
METALLURGICAL AND MATERIALS TRANSACTIONS B-PROCESS METALLURGY AND MATERIALS PROCESSING SCIENCE, 2011, 42 (05) :921-924
[9]   Inclusion composition control in tyre cord steel by top slag refining [J].
He, X. F. ;
Wang, X. H. ;
Chen, S. H. ;
Jiang, M. ;
Huang, F. X. ;
Wang, W. J. .
IRONMAKING & STEELMAKING, 2014, 41 (09) :676-684
[10]   Thermodynamics on the formation of spinel nonmetallic inclusion in liquid steel [J].
Itoh, H ;
Hino, M ;
BanYa, S .
METALLURGICAL AND MATERIALS TRANSACTIONS B-PROCESS METALLURGY AND MATERIALS PROCESSING SCIENCE, 1997, 28 (05) :953-956