Nano and macro tribology of elastomers

被引:20
作者
Bistac, S [1 ]
Galliano, A [1 ]
机构
[1] CNRS, ICSI, F-68057 Mulhouse, France
关键词
tribology; friction; elastomer; PDMS;
D O I
10.1007/s11249-004-1701-y
中图分类号
TQ [化学工业];
学科分类号
0817 ;
摘要
The friction of polydimethylsiloxane (PDMS) elastomers is quantified at two different scales: at the macroscopic scale with a tribometer, and at the nanoscopic scale, using atomic force microscopy (AFM). The objective is firstly to verify if friction behaviours are comparable at both scales, and secondly to define molecular mechanisms to be able to explain the measured properties.
引用
收藏
页码:21 / 25
页数:5
相关论文
共 11 条
[1]   INFLUENCE OF PENDANT CHAINS ON THE LOSS MODULUS OF MODEL NETWORKS [J].
BIBBO, MA ;
VALLES, EM .
MACROMOLECULES, 1984, 17 (03) :360-365
[2]   Separation rate dependence of adherence strength [J].
Bistac, S .
JOURNAL OF COLLOID AND INTERFACE SCIENCE, 1999, 219 (01) :210-211
[3]   Chains anisotropy in PDMS networks due to friction on cold surfaces [J].
Elzein, T ;
Galliano, A ;
Bistac, S .
JOURNAL OF POLYMER SCIENCE PART B-POLYMER PHYSICS, 2004, 42 (12) :2348-2353
[4]   Adhesion and friction of PDMS networks: molecular weight effects [J].
Galliano, A ;
Bistac, S ;
Schultz, J .
JOURNAL OF COLLOID AND INTERFACE SCIENCE, 2003, 265 (02) :372-379
[5]   The role of free chains in adhesion and friction of poly(dimethylsiloxane) (PDMS) networks [J].
Galliano, A ;
Bistac, S ;
Schultz, J .
JOURNAL OF ADHESION, 2003, 79 (10) :973-991
[6]   EFFECT OF WETTING LIQUIDS ON STRENGTH OF ADHESION OF VISCOELASTIC MATERIALS [J].
GENT, AN ;
SCHULTZ, J .
JOURNAL OF ADHESION, 1972, 3 (04) :281-&
[7]   RELATIONSHIP BETWEEN THE COHESIVE STRENGTH AND THE TACK OF ELASTOMERS [J].
HAMED, GR ;
SHIEH, CH .
JOURNAL OF POLYMER SCIENCE PART B-POLYMER PHYSICS, 1983, 21 (08) :1415-1425
[8]   Tribology of shearing polymer surfaces. 1. Mica sliding on polymer (PnBMA) [J].
Heuberger, M ;
Luengo, G ;
Israelachvili, JN .
JOURNAL OF PHYSICAL CHEMISTRY B, 1999, 103 (46) :10127-10135
[9]   STUDY OF THE SELF-ADHESION HYSTERESIS OF A SILOXANE ELASTOMER USING THE JKR METHOD [J].
SILBERZAN, P ;
PERUTZ, S ;
KRAMER, EJ ;
CHAUDHURY, MK .
LANGMUIR, 1994, 10 (07) :2466-2470
[10]   RELATION BETWEEN ADHESION AND FRICTION FORCES ACROSS THIN-FILMS [J].
YOSHIZAWA, H ;
ISRAELACHVILI, J .
THIN SOLID FILMS, 1994, 246 (1-2) :71-76