Low-temperature selective catalytic reduction of NOx with NH3 over an activated carbon-carbon nanotube composite material prepared by in situ method

被引：24

作者：

Wang, Pengchen ^{[1
]}

Yao, Lu ^{[1
]}

Pu, Yijuan ^{[2
]}

Yang, Lin ^{[1
,2
]}

Jiang, Xia ^{[1
,2
]}

Jiang, Wenju ^{[1
,2
]}

机构：

[1] Sichuan Univ, Coll Architecture & Environm, Chengdu 610065, Sichuan, Peoples R China

[2] Natl Engn Res Ctr Flue Gas Desulfurizat, Chengdu 610065, Sichuan, Peoples R China

来源：

RSC ADVANCES | 2019年 / 9卷 / 63期

基金：

中国博士后科学基金;

关键词：

SUPERIOR CATALYST; NH3-SCR; PERFORMANCE; REMOVAL; OXIDES; CERIA; CNTS; MNOX; SCR;

D O I：

10.1039/c9ra08640d

中图分类号：

O6 [化学];

学科分类号：

0703 ;

摘要：

Ce-supported activated carbon-carbon nanotube composite (Ce/AC-CNTs) catalyst was prepared by in situ formation of CNTs on AC and then modified by Ce. This Ce/AC-CNTs catalyst was subsequently used for low-temperature selective catalytic reduction of NOx with NH3 (NH3-SCR). The NO conversion of Ce/AC-CNTs was 1.41 times higher than that of Ce/AC at 150 degrees C with good SO2 tolerance. The catalysts were analyzed by N-2 physisorption, SEM, XRD, NH3-TPD, XPS, and Raman technologies. The results showed that the introduction of CNTs could form new mesopores and increase the amount of surface chemisorbed oxygen and acid sites, which all contribute to the high NH3-SCR activity.

引用

页码：36658 / 36663

页数：6

共 50 条

[1] Low-temperature selective catalytic reduction of NOx with NH3 over a manganese and cerium oxide/graphene composite prepared by a hydrothermal method
Xiao, Xiang
Sheng, Zhongyi
Yang, Liu
Dong, Fan
CATALYSIS SCIENCE & TECHNOLOGY, 2016, 6 (05) : 1507 - 1514
[2] In situ supported MnOx-CeOx on carbon nanotubes for the low-temperature selective catalytic reduction of NO with NH3
Zhang, Dengsong
Zhang, Lei
Shi, Liyi
Fang, Cheng
Li, Hongrui
Gao, Ruihua
Huang, Lei
Zhang, Jianping
NANOSCALE, 2013, 5 (03) : 1127 - 1136
[3] Regeneration of field-spent activated carbon catalysts for low-temperature selective catalytic reduction of NOx with NH3
Jeon, Jong-Ki
Kim, Hyeonjoo
Park, Young-Kwon
Peden, Charles H. F.
Kim, Do Heui
CHEMICAL ENGINEERING JOURNAL, 2011, 174 (01) : 242 - 248
[4] Selective catalytic reduction of NO with NH3 over activated carbon impregnated with melamine at low temperature
Li, Qiao-Yan
Hou, Ya-Qin
Han, Xiao-Jin
Huang, Zhang-Gen
Guo, Qian-Qian
Sun, De-Kui
Liu, Jian-Dong
Ranliao Huaxue Xuebao/Journal of Fuel Chemistry and Technology, 2014, 42 (04): : 487 - 493
[5] Low-temperature selective catalytic reduction of NOx with NH3 over MnFeOx nanorods
Li, Yi
Li, Yanping
Wang, Pengfei
Hu, Wenping
Zhang, Suge
Shi, Qiang
Zhan, Sihui
CHEMICAL ENGINEERING JOURNAL, 2017, 330 : 213 - 222
[6] Low-temperature selective catalytic reduction of NO with NH3 over nanoflaky MnOx on carbon nanotubes in situ prepared via a chemical bath deposition route
Fang, Cheng
Zhang, Dengsong
Cai, Sixiang
Zhang, Lei
Huang, Lei
Li, Hongrui
Maitarad, Phornphimon
Shi, Liyi
Gao, Ruihua
Zhang, Jianping
NANOSCALE, 2013, 5 (19) : 9199 - 9207
[7] Preparation of MnOx/CNTs Catalyst by In situ Precipitation Method for Low-Temperature NO Reduction with NH3
Zhang, Yanbing
Chen, Yingzan
Huang, Jinhe
Ding, Mingjie
Li, Xiaoyan
Zhao, Haipeng
CURRENT NANOSCIENCE, 2021, 17 (02) : 298 - 306
[8] Low-temperature selective catalytic reduction of NOx with NH3 over Mn-containing catalysts
Stanciulescu, M.
Caravaggio, G.
Dobri, A.
Moir, J.
Burich, R.
Charland, J. -P.
Bulsink, P.
APPLIED CATALYSIS B-ENVIRONMENTAL, 2012, 123 : 229 - 240
[9] The effect of the oxidation method of an activated carbon on the selective catalytic reduction of NOx with NH3 over CeO2/activated carbon catalysts
Huang Li-hua
Li Xue
Chen Yao-qiang
NEW CARBON MATERIALS, 2018, 33 (03) : 237 - 244
[10] Low-temperature selective catalytic reduction of NOx with NH3 over zeolite catalysts: A review
Pu, Yijuan
Xie, Xinyu
Jiang, Wenju
Yang, Lin
Jiang, Xia
Yao, Lu
CHINESE CHEMICAL LETTERS, 2020, 31 (10) : 2549 - 2555

← 1 2 3 4 5 →