The influence of lithia content on the properties of fluorphlogopite glass-ceramics. II. Microstructure hardness and machinability

被引：44

作者：

Henry, J

Hill, RG ^{[1
]}

机构：

[1] Univ London Imperial Coll Sci Technol & Med, Dept Mat, London SW7 2BP, England

[2] Univ Limerick, Dept Mat Sci & Technol, Limerick, Ireland

来源：

JOURNAL OF NON-CRYSTALLINE SOLIDS | 2003年 / 319卷 / 1-2期

关键词：

D O I：

10.1016/S0022-3093(02)01959-2

中图分类号：

TQ174 [陶瓷工业]; TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

The influence of heat treatment time and temperature on microstructure, hardness and theoretical machinability of glass-ceramics based on 8SiO(2) 3Al(2)O(3) (3 - S)MgO 3MgF(2) (1 - Z)BaOZK(2)OSLi(2)O where lithia was substituted for magnesia and baria for potassia were investigated. Lithia and potassia were found to promote the crystal coarsening of the fluorphlogopite phase and the development of a house of cards microstructure. Hardness was found to decrease slightly on formation of the fluorphlogopite phase, but to decrease markedly on development of the house of cards microstructure. The formation of the house of cards microstructure was promoted by heat treatments close to the observed melting endotherms and was associated with good machinability. Incorporation of lithia was found to suppress the formation of, cordierite in the bulk. (C) 2003 Elsevier Science B.V. All rights reserved.

引用

页码：13 / 30

页数：18

共 25 条

[1] A COMPARATIVE-EVALUATION METHOD OF MACHINABILITY FOR MICA-BASED GLASS-CERAMICS [J].