Research on the Oxidation Mechanism of Vermicular Graphite Cast Iron

被引：15

作者：

Guo, Qiaoqin ^{[1
]}

Yang, Zhong ^{[1
]}

Guo, Ding ^{[2
]}

Tao, Dong ^{[1
]}

Guo, Yongchun ^{[1
]}

Li, Jianping ^{[1
]}

Bai, Yaping ^{[1
]}

机构：

[1] Xian Technol Univ, Sch Mat & Chem Engn, Xian 710032, Shaanxi, Peoples R China

[2] Xian Capital Water Ltd Co, Xian 710086, Shaanxi, Peoples R China

来源：

MATERIALS | 2019年 / 12卷 / 19期

基金：

中国国家自然科学基金;

关键词：

oxidation mechanism; vermicular graphite iron; oxidation channel; graphite; scanning electron microscope (SEM); HIGH-TEMPERATURE OXIDATION; THERMAL BARRIER COATINGS; RESISTANCE; SURFACE; ALLOY; LAYER; MICROSTRUCTURE; GROWTH; OXIDE; WEAR;

D O I：

10.3390/ma12193130

中图分类号：

O64 [物理化学（理论化学）、化学物理学];

学科分类号：

070304 ; 081704 ;

摘要：

The oxidation mechanism of vermicular graphite cast iron was studied. The oxidation reaction starts from graphites and diffused slowly. Graphites in vermicular graphite are interconnected, coral-like clusters, providing the main oxidation core and channel. The worm-like graphites on the surface are mostly oxidized and form oxide affected zones. The oxide films are composed of a loose oxide layer with the phases of Fe3O4, Fe2O3, and FeO, and a dense passivation layer with FeO and Fe2SiO4. After oxidation, pearlites in the vermicular graphite cast iron are decomposed into ferrite and cementite at high temperatures.

引用

页数：8

共 31 条

[1] Effect of coating thickness on the tool wear performance of low stress TiAlN PVD coating during turning of compacted graphite iron (CGI) [J].

Abdoos, Majid ;

Yamamoto, Kenji ;

Bose, Bipasha ;

Fox-Rabinovich, German ;

Veldhuis, Stephen .

WEAR, 2019, 422 :128-136

[2] Effect of graphite morphology on the fatigue and fracture resistance of ferritic ductile cast iron [J].

Benedetti, M. ;

Fontanari, V ;

Lusuardi, D. .

ENGINEERING FRACTURE MECHANICS, 2019, 206 :427-441

[3] The effect of manganese additions on the high temperature oxidation behaviour of the high-vanadium cast iron [J].

Chen, Pinghu ;

Liu, Zhilin ;

Li, Ruiqing ;

Li, Xiaoqian .

JOURNAL OF ALLOYS AND COMPOUNDS, 2018, 767 :181-187

[4] Formation of a dense and continuous Al2O3 layer in nano thermal barrier coating systems for the suppression of spinel growth on the Al2O3 oxide scale during oxidation [J].

Daroonparvar, Mohammadreza ;

Yajid, Muhamad Azizi Mat ;

Yusof, Noordin Mohd ;

Hussain, Mohammad Sakhawat ;

Bakhsheshi-Rad, Hamid Reza .

JOURNAL OF ALLOYS AND COMPOUNDS, 2013, 571 :205-220

[5]

Dawson S, 2009, CHINA FOUNDRY, V6, P241

[6] High temperature oxidation resistance of M42C stainless steel coatings deposited on the surface of cast iron through atmospheric plasma spraying [J].

Gao, Pei-Hu ;

Cao, Si-Ting ;

Li, Jian-Ping ;

Yang, Zhong ;

Guo, Yong-Chun ;

Wang, Yan-Rong .

JOURNAL OF ALLOYS AND COMPOUNDS, 2016, 684 :188-194

[7] Study on microstructure and tribological properties of AlSn films deposited via magnetron sputtering ion plating [J].

Guo, Qiao-qin ;

Guo, Yong-chun ;

Yang, Zhong ;

Li, Jian-ping ;

Xu, Guang-tao .

APPLIED SURFACE SCIENCE, 2019, 483 :123-132

[8] Effects of vermicular graphite rate on the oxidation resistance and mechanical properties of vermicular graphite iron [J].

Guo, Qiaoqin ;

Zhong, Yang ;

Dong, Tao ;

Gao, Peihu ;

Guo, Yongchun ;

Li, Jianping .

JOURNAL OF ALLOYS AND COMPOUNDS, 2018, 765 :213-220

[9] Residual stress evolution of thermally grown oxide in thermal barrier coatings deposited onto nickel-base superalloy and iron-base alloy with thermal exposure ageing [J].

Han, Y. J. ;

Ye, F. X. ;

Lu, G. X. ;

Liu, C. ;

Hao, L. J. .

JOURNAL OF ALLOYS AND COMPOUNDS, 2014, 584 :19-27

[10]

Hecht R.I., 2013, J MATER SCI, V34, P4775

← 1 2 3 4 →