An experimental study on crack closure induced by laser peening in pre-cracked aluminum alloy 2024-T351 and fatigue life extension

被引：39
|
作者：
Hu, Yongxiang [1 ]
Cheng, Han [1 ]
Yu, Jianhua [1 ,2 ]
Yao, Zhenqiang [1 ]
机构：
[1] Shanghai Jiao Tong Univ, Sch Mech Engn, State Key Lab Mech Syst & Vibrat, Shanghai 200240, Peoples R China
[2] AECC Commercial Aircraft Engine Co Ltd, Shanghai 200240, Peoples R China
来源：
INTERNATIONAL JOURNAL OF FATIGUE | 2020年 / 130卷
关键词：
Laser peening; Damage; Fatigue crack propagation; Crack closure; Crack arrest; DIGITAL IMAGE CORRELATION; RESIDUAL-STRESS; GROWTH-PROPERTIES; MICROSTRUCTURE; DAMAGE; PROPAGATION; BEHAVIOR; MODEL; STEEL;
D O I：
10.1016/j.ijfatigue.2019.105232
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
This study investigates crack closure induced by laser peening (LP) and its effect on fatigue life extension of 2024-T351 aluminum alloy with initial fatigue crack. LP is applied directly in the initial fatigue crack region. This treatment leads to interesting observations of crack arrest that has not been reported before for LP, and significant fatigue life enhancement. The fatigue life of the LP-treated pre-cracked specimen is 412% and 44.7% higher than the untreated specimen and LP-treated specimen without pre-crack, respectively. The crack closure around the pre-crack resulting from the LP-induced plastic deformation is mainly responsible for fatigue life extension.
引用
收藏
页数：10
相关论文
共 50 条
  • [41] Experimental study on the effect of dents induced by impact on the fatigue life of 2024-T3 aluminum alloy plate
    Li, Zhigang
    Feng, Rongxin
    Wang, Yan
    Wang, Lishu
    ENGINEERING STRUCTURES, 2017, 137 : 236 - 244
  • [42] Mechanical properties and microstructure characteristics of 2024-T351 aluminum alloy specimen subjected to paint removal by laser cleaning
    Sun, Qi
    Zhou, Jianzhong
    Meng, Xiankai
    Li, Pengfei
    VACUUM, 2023, 211
  • [43] Effects of laser peening with different coverage areas on fatigue crack growth properties of 6061-T6 aluminum alloy
    Huang, S.
    Zhou, J. Z.
    Sheng, J.
    Luo, K. Y.
    Lu, J. Z.
    Xu, Z. C.
    Meng, X. K.
    Dai, L.
    Zuo, L. D.
    Ruan, H. Y.
    Chen, H. S.
    INTERNATIONAL JOURNAL OF FATIGUE, 2013, 47 : 292 - 299
  • [44] Effect of elastic prestress on the laser peen forming of aluminum alloy 2024-T351: Experiments and eigenstrain-based modeling
    Hu, Yongxiang
    Li, Zhi
    Yu, Xiongchao
    Yao, Zhenqiang
    JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2015, 221 : 214 - 224
  • [45] On small fatigue crack growth and crack closure under mixed-mode and through zero loading in the aluminium alloys 2024-T351 and 8090-T8771
    Halliday, M. D.
    Cooper, C.
    Bowen, P.
    INTERNATIONAL JOURNAL OF FATIGUE, 2007, 29 (07) : 1195 - 1207
  • [46] Experimental investigation and numerical prediction of fatigue crack growth of 2024-T4 aluminum alloy
    Wang, Cheng
    Wang, Xiaogui
    Ding, Zhenyu
    Xu, Yangjian
    Gao, Zengliang
    INTERNATIONAL JOURNAL OF FATIGUE, 2015, 78 : 11 - 21
  • [47] Study on fatigue crack growth performance of 6061-T6 aluminum alloy after laser shot peening
    Zhou J.
    Wang C.
    Huang S.
    Yang X.
    Xu Z.
    Yang J.
    Zhu W.
    Zhongguo Jiguang/Chinese Journal of Lasers, 2011, 38 (07):
  • [48] Random-type scanning patterns in laser shock peening without absorbing coating in 2024-T351 Al alloy: A solution to reduce residual stress anisotropy
    Correa, C.
    Peral, D.
    Porro, J. A.
    Diaz, M.
    Ruiz de Lara, L.
    Garcia-Beltran, A.
    Ocana, J. L.
    OPTICS AND LASER TECHNOLOGY, 2015, 73 : 179 - 187
  • [49] Experimental investigation of fatigue crack initiation from notches in 2024 T351 Al-alloy
    Benachour, Nadjia
    Benachour, Mustapha
    Benguediab, Mohamed
    FRATTURA ED INTEGRITA STRUTTURALE, 2020, 14 (51): : 45 - 51
  • [50] An experimental methodology to quantify the resistance of grain boundaries to fatigue crack growth in an AA2024 T351 Al-Cu Alloy
    Wen, Wei
    Cai, Pei
    Ngan, Alfonso H. W.
    Zhai, Tongguang
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2016, 666 : 288 - 296
12345