Aging of an Fe-Ni-Al alloy in magnetic field

被引：1

作者：

Ohtsuka, H

Ghosh, G

Mamiya, H

Wada, H

机构：

[1] Natl Res Inst Met, Tsukuba Magnet Lab, Tsukuba, Ibaraki 305, Japan

[2] Northwestern Univ, Dept Mat Sci & Engn, Evanston, IL 60208 USA

[3] Natl Res Inst Met, Res Grp 4, Tsukuba, Ibaraki 305, Japan

来源：

JOURNAL OF THE JAPAN INSTITUTE OF METALS | 1997年 / 61卷 / 12期

关键词：

iron-23.3nickel-9.4aluminum (mass%) alloy; aging in magnetic field; spinodal decomposition; ordering; precipitation magnetic moment;

D O I：

10.2320/jinstmet1952.61.12_1333

中图分类号：

TF [冶金工业];

学科分类号：

0806 ;

摘要：

Aging of an Fe-23.3Ni-9.4Al (mass%) alloy was carried out both in the presence of a magnetic field (9 T) and without a magnetic field at 673, 773, 873 and 973 K for 5 h. The saturation magnetic moment of the samples were measured at 200, 100, 50 and 5 K and extrapolated to 0 K. A systematic difference in average magnetic moment is observed between the samples aged with and without magnetic field. Except for aging at 773 K, the average magnetic moment of the samples aged under magnetic field is smaller than those aged without a magnetic field. TEM observation showed the evidence of spinodal decomposition of disordered bcc (A2) and ordered bcc (B2) phases. The difference in magnetic moments is attributed to the difference in kinetics of ordering/decomposition due to the magnetic field.

引用

页码：1333 / 1336

页数：4