Effect of Optical Properties of Lithium Disilicate Glass Ceramics and Light-Curing Protocols on the Curing Performance of Resin Cement

This study aimed to investigate the effects of optical properties of lithium disilicate glass ceramics and the light-curing protocols (LCP) on the curing performance of light-cured resin cement. Lithium disilicate glass-ceramics with different optical properties were sectioned to produce ceramic specimens of 0.8 mm thickness. Irradiance through the ceramic specimens was measured by a radiometer. Light transmittance of ceramics was assessed using a UV/Vis spectrophotometer. The light-cured resin cement was injected into a Teflon mold and ceramics with different optical properties were placed on it, cured under different LCPs, and the degree of conversion (DC) and Vickers microhardness of the resin cement were separately measured by Micro-ATR/FTIR spectrometry and the microhardness tester. The shade (p < 0.001) and transparency (p < 0.001) of ceramics affect the irradiance of the light-curing unit. The transparency (p < 0.001) of the ceramic and light-curing protocols (p < 0.001) affect the DC and microhardness of resin cements. When the thickness of the ceramic is 0.8 mm, the light transmittance of the ceramic and the curing performance of the resin cement increase with the increase of the transparency of the ceramic. An appropriate increase in irradiance and exposure time can optimize the curing performance of resin cement. These factors should be taken into account by the clinician when designing the bonding solution for porcelain veneers.