The formation of different phases of CuxTe and their effects on CdTe/CdS solar cells

被引:78
作者
Zhou, J. [1 ]
Wu, X.
Duda, A.
Teeter, G.
Demtsu, S. H.
机构
[1] NREL, Golden, CO 80401 USA
[2] Colorado State Univ, Dept Phys, Ft Collins, CO 80523 USA
关键词
cadmium telluride; copper telluride; back contact; solar cells;
D O I
10.1016/j.tsf.2007.03.032
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
Material studies and device applications of CuxTe in an NREL-developed CdTe solar cell structured as glass/Cd2SnO4/ZnSnOx/CdS/CdTe are presented. The CuxTe primary back contact was formed by evaporating a Cu layer with various thicknesses at room temperature on HNO3/H3PO4 (NP) solution etched CdTe layer. A post-annealing was then followed. The structural evolution and electrical properties of CuxTe were investigated. Cu/Te ratio and post-annealing temperature are two processing parameters in this study The CuxTe phases are mainly controlled by the Cu/Te ratio. After a post-annealing at a low temperature, such as 100 degrees C, no CqTe phase transformation from its as-deposited phase was observed. A post-annealing treatment at a higher temperature, such as 250 degrees C, can reveal the stoichiometric CuxTe phases based on the Cu/Te ratio used in the devices. But a post-annealing at a further higher temperature, such as 400 degrees C, resulted in a complicated CqTe phase appearance. CuTe, CU1,4Te, and CU2Te are three major phases detected by X-ray diffraction (XRD) for different Cu thickness application annealed at 250 degrees C. Application of Cu thicker than 60 nm degrades open-circuit voltage (V-oc) and shunting resistance (R-sh), but increases series resistance (R-s). The correlation between device performance and the CuxTe back contact illustrates that the process used for forming the CU2Te back contact failed to produce good fill factor (FF) and also introduced higher barrier height. The best device was observed for a back contact with a mixed CU1.4Te and CuTe phases. Published by Elsevier B.V.
引用
收藏
页码:7364 / 7369
页数:6
相关论文
共 16 条
[1]  
ASTAKHOV OP, 1973, IZVESTIYA AKAD PTCGS, V4, P108
[2]   EFFECTS OF CU ON CDTE/CDS HETEROJUNCTION SOLAR-CELLS WITH AU/CU CONTACTS [J].
CHOU, HC ;
ROHATGI, A ;
THOMAS, EW ;
KAMRA, S ;
BHAT, AK .
JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1995, 142 (01) :254-259
[3]   13.4-PERCENT EFFICIENT THIN-FILM CDS/CDTE SOLAR-CELLS [J].
CHU, TL ;
CHU, SS ;
FEREKIDES, C ;
WU, CQ ;
BRITT, J ;
WANG, C .
JOURNAL OF APPLIED PHYSICS, 1991, 70 (12) :7608-7612
[4]   Some annealing effects on rf sputtered Cu/Te/CdTe structure [J].
Debbagh, F ;
Ameziane, EL ;
Azizan, M ;
Brunel, M ;
Nguyen, TTA .
MATERIALS SCIENCE AND ENGINEERING B-SOLID STATE MATERIALS FOR ADVANCED TECHNOLOGY, 1996, 38 (03) :223-227
[5]   Effect of back-contact barrier on thin-film CdTe solar cells [J].
Demtsu, S. H. ;
Sites, J. R. .
THIN SOLID FILMS, 2006, 510 (1-2) :320-324
[6]   Photoluminescence study of Cu diffusion and electromigration in CdTe [J].
Grecu, D ;
Compaan, AD .
APPLIED PHYSICS LETTERS, 1999, 75 (03) :361-363
[7]   CdTe contacts for CdTe/CdS solar cells: effect of Cu thickness, surface preparation and recontacting on device performance and stability [J].
Hegedus, SS ;
McCandless, BE .
SOLAR ENERGY MATERIALS AND SOLAR CELLS, 2005, 88 (01) :75-95
[8]   Analysis of stress-induced degradation in CdS/CdTe solar cells [J].
Hegedus, SS ;
McCandless, BE ;
Birkmire, RW .
CONFERENCE RECORD OF THE TWENTY-EIGHTH IEEE PHOTOVOLTAIC SPECIALISTS CONFERENCE - 2000, 2000, :535-538
[9]   Correlation of surface phases with electrical behavior in thin-film CdTe devices [J].
McCandless, BE ;
Hegedus, SS ;
Birkmire, RW ;
Cunningham, D .
THIN SOLID FILMS, 2003, 431 :249-256
[10]   Processing options for CdTe thin film solar cells [J].
McCandless, BE ;
Dobson, KD .
SOLAR ENERGY, 2004, 77 (06) :839-856