The Effect of Cryo-Rolling and Annealing on Magnetic Properties in Non-Oriented Electrical Steel

The goal of the present work is to compare progressive technology - rolling at cryogenic temperature and classical rolling at ambient temperature followed by an investigation of their impact on the final microstructure and the magnetic properties of non-oriented electrical steel. Non-oriented electrical steel is characterized by high magnetic induction, low magnetic losses, and low coercivity. The best magnetic properties are achieved using preferable texture and optimal grain size. In this paper there is analyzed the percentage of different textural components after cryo-rolling and after rolling at ambient temperature. To obtain maps of inverse pole figures, the electron backscatter diffraction method was used. The main contribution of this study was that the samples rolled at cryo conditions and after final annealing reached better magnetic properties than at ambient temperature, which was reflected by low magnetic losses and coercivity.