Stability of MnCr2O4 spinel and Cr2O3 in high temperature carbonaceous environments with varied oxygen partial pressures

被引：73

作者：

Li, Hao ^{[1
]}

Chen, Weixing ^{[1
]}

机构：

[1] Univ Alberta, Dept Chem & Mat Engn, Edmonton, AB T6G 2V4, Canada

来源：

CORROSION SCIENCE | 2010年 / 52卷 / 07期

基金：

加拿大自然科学与工程研究理事会;

关键词：

Ceramic; SEM; XRD; Weight loss; Carburization; Oxidation; OXIDIZING/CARBURIZING ENVIRONMENT; HK40; ALLOY; CARBURIZATION; MANGANESE; CHROMIUM; OXIDATION; MICROSTRUCTURE; SERVICE; GROWTH; SYSTEM;

D O I：

10.1016/j.corsci.2010.02.040

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

In this investigation, Cr2O3 and MnCr2O4 were comparatively tested at 1050 degrees C in carbonaceous environment with varied oxygen partial pressures. MnCr2O4 exhibits much better resistance to carbonaceous attack than Cr2O3. The carburization rate of MnCr2O4 decreases sharply with increasing oxygen partial pressures. The oxygen partial pressures have less effect on the carburization resistance of Cr2O3. The increased resistance of MnCr2O4 to carburization is attributed to the dissolution of MnO into Mn-Cr-O spinel lattices with elevated oxygen partial pressures, which retards the decomposition and carburization of Mn-Cr-O spinel. The thermodynamic equations defining the carburization stability of MnCr2O4 and Cr2O3 are modified. (C) 2010 Elsevier Ltd. All rights reserved.

引用

页码：2481 / 2488

页数：8

共 30 条

[1]

BENUM L, 2005, Patent No. 6824883

[2] THE CONVERSION OF CHROMIUM-OXIDE TO CHROMIUM CARBIDE [J].

CHU, WF ;

RAHMEL, A .

OXIDATION OF METALS, 1981, 15 (3-4) :331-337

[3] OXIDATION OF MANGANESE IN CO2-CO MIXTURES [J].

FUEKI, K ;

WAGNER, JB .

JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1965, 112 (10) :970-&

[4]

Garbers-Craig AM, 1998, J AM CERAM SOC, V81, P933, DOI 10.1111/j.1151-2916.1998.tb02429.x

[5]

Gaskell D. R., 2017, Introduction to the Thermodynamics of Materials

[6]

Grabke H.J., 1998, Carburization: A High Temperature Corrosion Phenomenon, V1st ed.

[7] CARBURIZATION AND OXIDATION [J].

GRABKE, HJ ;

WOLF, I .

MATERIALS SCIENCE AND ENGINEERING, 1987, 87 (1-2) :23-33

[8] The effect of manganese additions on the reactive evaporation of chromium in Ni-Cr alloys [J].

Holcomb, GR ;

Alman, DE .

SCRIPTA MATERIALIA, 2006, 54 (10) :1821-1825

[9] GAS METAL REACTIONS OF A NEW FE-NI-CR-W ALLOY IN HELIUM WITH REACTIVE COMPONENTS AND IN AN H-2-CH4-H2S ATMOSPHERE IN THE TEMPERATURE-RANGE 700-950-DEGREES-C [J].

HUCHTEMANN, B ;

SCHULER, P .

MATERIALS SCIENCE AND ENGINEERING, 1987, 87 (1-2) :197-203

[10] Microstructure of HK40 alloy after high-temperature service in oxidizing/carburizing environment - II. Carburization and carbide transformations [J].

Kaya, AA .

MATERIALS CHARACTERIZATION, 2002, 49 (01) :23-34

← 1 2 3 →