Effects of processing parameters on liquation cracking of 6005A alloy weldments

被引：2
|
作者：
Choi, JH
Lee, DH
Kim, J
Shin, DH
Kim, YS
机构：
[1] Hongik Univ, Dept Met & Mat Sci, Seoul 121791, South Korea
[2] Dongyang Gangchul, R&D Ctr, Taejon 306020, South Korea
[3] Hanyang Univ, Dept Met & Mat Engn, Ansam 425791, South Korea
来源：
METALS AND MATERIALS-KOREA | 2000年 / 6卷 / 04期
关键词：
6005A aluminum alloy; extrusion; weldment; liquation cracking;
D O I：
10.1007/BF03028088
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The effects of the characteristic microstructure developed in extruded 6005A alloys on tensile properties, fatigue strength, and liquation cracking in the heat affected zone of weldments were investigated, An insitu observation of the grain growth occurring in the sample was made with an optical microscope with a hot stage to determine the temperature of the excessive grain growth during extrusion. The extruded samples were heat heated under various conditions and welded using a gas metal arc welding process. The results indicated that liquation occurred mainly at coarse grain boundaries and significantly influencing the mechanical properties of the joint.
引用
收藏
页码：395 / 399
页数：5
相关论文
共 50 条
  • [21] Liquation cracking in laser beam welded joint of ZK60 magnesium alloy
    Yu Zhao-hui
    Yan Hong-ge
    Yin Xu-yu
    Li Ying
    Yan Guo-hua
    TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2012, 22 (12) : 2891 - 2897
  • [22] Microstructure and Mechanical Properties of an Extruded 6005A Al Alloy Composite Reinforced with TiC Nanosized Particles and Strengthened by Precipitation Hardening
    Feijoo, Iria
    Merino, Pedro
    Pena, Gloria
    Rey, Pilar
    Cabeza, Marta
    METALS, 2020, 10 (08) : 1 - 15
  • [23] Effect of Solution Annealing Temperature on Liquation Cracking Susceptibility of Alloy 617M
    Divya, M.
    Mahata, C.
    Pradeep, K. G.
    Das, C. R.
    Vasudevan, M.
    METALS AND MATERIALS INTERNATIONAL, 2024, 30 (08) : 2215 - 2228
  • [24] Liquation cracking of Al-6.3 Cu alloy propellant storage tank - A case study
    Jha, Abhay K.
    Narayanan, P. Ramesh
    Sreekumar, K.
    ENGINEERING FAILURE ANALYSIS, 2009, 16 (05) : 1587 - 1596
  • [25] Liquation cracking behavior and control in the heat affected zone of GH909 alloy during Nd: YAG laser welding
    Yan, Fei
    Liu, Sang
    Hu, Chongjing
    Wang, Chunming
    Hu, Xiyuan
    JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2017, 244 : 44 - 50
  • [26] Effects of Al/Zn interlayer on the solidification path and liquation cracking susceptibility of AZ31/ZK61 dissimilar magnesium alloy resistance spot welding joints
    Zhang, Yu
    Zhou, Zuyu
    Fu, Yiqin
    Li, Hong
    Li, Zhuoxin
    Mariusz, Bober
    Senkara, Jacek
    JOURNAL OF MANUFACTURING PROCESSES, 2022, 75 : 60 - 71
  • [27] Effects of pre- and post-weld heat treatment cycles on the liquation and strain-age cracking of IN939 superalloy
    Kazempour-Liasi, H.
    Tajally, M.
    Abdollah-Pour, H.
    ENGINEERING RESEARCH EXPRESS, 2019, 1 (02):
  • [28] Processing Effects on the Formability of Magnesium Alloy Sheets
    Bohlen, Jan
    Cano, Guadalupe
    Drozdenko, Daria
    Dobron, Patrik
    Kainer, Karl Ulrich
    Gall, Sven
    Mueller, Soeren
    Letzig, Dietmar
    METALS, 2018, 8 (02)
  • [29] Enhanced resistance to liquation cracking during fusion welding of cast magnesium alloys: Microstructure tailoring via friction stir processing pre-weld treatment
    Sharahi, H. Jiryaei
    Pouranvari, M.
    Movahedi, M.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2020, 798
  • [30] Dilution effects on weld metal microstructure and liquation cracking susceptibility of 304B4 SS joined using E309 electrode
    Divya, M.
    Albert, S. K.
    JOURNAL OF MANUFACTURING PROCESSES, 2018, 34 : 540 - 554
12345