Strain hardening behavior, strain rate sensitivity and hot deformation maps of AISI 321 austenitic stainless steel

被引:10
作者
Ghazani, Mehdi Shaban [1 ]
Eghbali, Beitallah [2 ]
机构
[1] Univ Bonab, Dept Mat Sci Engn, Bonab 5551761167, Iran
[2] Sahand Univ Technol, Fac Mat Engn, Tabriz 513351996, Iran
关键词
strain hardening; strain rate sensitivity; processing map; AISI 321 austenitic stainless steel; hot compression; PROCESSING MAPS; SUPERPLASTICITY; INSTABILITY;
D O I
10.1007/s12613-020-2163-4
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
Hot compression tests were performed on AISI 321 austenitic stainless steel in the deformation temperature range of 800-1200 degrees C and constant strain rates of 0.001, 0.01, 0.1, and 1 s(-1). Hot flow curves were used to determine the strain hardening exponent and the strain rate sensitivity exponent, and to construct the processing maps. Variations of the strain hardening exponent with strain were used to predict the microstructural evolutions during the hot deformation. Four variations were distinguished reflecting the different microstructural changes. Based on the analysis of the strain hardening exponent versus strain curves, the microstructural evolutions were dynamic recovery, single and multiple peak dynamic recrystallization, and interactions between dynamic recrystallization and precipitation. The strain rate sensitivity variations at an applied strain of 0.8 and strain rate of 0.1 s(-1) were compared with the microstructural evolutions. The results demonstrate the existence of a reliable correlation between the strain rate sensitivity values and evolved microstructures. Additionally, the power dissipation map at the applied strain of 0.8 was compared with the resultant microstructures at predetermined deformation conditions. The microstructural evolutions strongly correlated to the power dissipation ratio, and dynamic recrystallization occurred completely at lower power dissipation ratios.
引用
收藏
页码:1799 / 1810
页数:12
相关论文
共 25 条
[1]   Plastic strain localization in metals: origins and consequences [J].
Antolovich, Stephen D. ;
Armstrong, Ronald W. .
PROGRESS IN MATERIALS SCIENCE, 2014, 59 :1-160
[2]   High strain rate superplasticity in a commercial 2024 Al alloy via friction stir processing [J].
Charit, I ;
Mishra, RS .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2003, 359 (1-2) :290-296
[4]   Characterization of the hot deformation microstructure of AISI 321 austenitic stainless steel [J].
Ghazani, M. Shaban ;
Eghbali, B. .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2018, 730 :380-390
[5]   A Ductile Damage Criterion for AISI 321 Austenitic Stainless Steel at Different Temperatures and Strain Rates [J].
Ghazani, Mehdi Shaban ;
Eghbali, Beitallah .
ARABIAN JOURNAL FOR SCIENCE AND ENGINEERING, 2018, 43 (09) :4855-4861
[6]   Evaluation of the Kinetics of Dynamic Recovery in AISI 321 Austenitic Stainless Steel Using Hot Flow Curves [J].
Ghazani, Mehdi Shaban ;
Eghbali, Beitallah ;
Ebrahimi, Gholam Reza .
TRANSACTIONS OF THE INDIAN INSTITUTE OF METALS, 2017, 70 (07) :1755-1761
[7]   INFLUENCE OF STRAIN-HARDENING AND STRAIN-RATE SENSITIVITY ON SHEET-METAL FORMING [J].
GHOSH, AK .
JOURNAL OF ENGINEERING MATERIALS AND TECHNOLOGY-TRANSACTIONS OF THE ASME, 1977, 99 (03) :264-274
[8]   TENSILE INSTABILITY AND NECKING IN MATERIALS WITH STRAIN-HARDENING AND STRAIN-RATE HARDENING [J].
GHOSH, AK .
ACTA METALLURGICA, 1977, 25 (12) :1413-1424
[9]   Research on Flow Stress During Hot Deformation Process and Processing Map for 316LN Austenitic Stainless Steel [J].
Guo, Baofeng ;
Ji, Haipeng ;
Liu, Xingang ;
Gao, Lu ;
Dong, Rongmei ;
Jin, Miao ;
Zhang, Qinghua .
JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2012, 21 (07) :1455-1461
[10]   Relationship between stretch formability and work-hardening capacity of twin-roll cast Mg alloys at room temperature [J].
Kang, D. H. ;
Kim, D. -W. ;
Kim, S. ;
Bae, G. T. ;
Kim, K. H. ;
Kim, Nack J. .
SCRIPTA MATERIALIA, 2009, 61 (07) :768-771