In situ observation of interactive failure modes in a single-edge notched symmetric cross-ply laminate using synchrotron X-ray tomography

被引：19

作者：

Jo, Eonyeon ^{[1
,2
]}

Lee, Sooyoung ^{[1
]}

Hong, Chaeyoung ^{[1
]}

Ji, Wooseok ^{[1
]}

机构：

[1] UNIST, Dept Mech Engn, Ulsan, South Korea

[2] LG Hausys R&D Ctr, Seoul, South Korea

来源：

COMPOSITES PART A-APPLIED SCIENCE AND MANUFACTURING | 2020年 / 128卷

基金：

新加坡国家研究基金会;

关键词：

Synchrotron radiation computed tomography; In situ testing; Interactive fracture behavior; DIC analysis; DAMAGE; COMPOSITES;

D O I：

10.1016/j.compositesa.2019.105661

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Interactive failure mechanisms of a single-edge notched (SEN) symmetric cross-ply laminate subjected to tensile loading are studied in situ using synchrotron X-ray tomography and a DIC technique at the micro- and macroscales. The SEN configuration guarantees the repeatability and consistency of the progressive and interactive failure behavior at the two different scales. The evolution of various fracture modes in different layers is observed through synchrotron radiation CT images. Due to the geometrically asymmetric configuration, all the initial cracks sequentially occurring near the notch tip can be captured in a narrow field of view. Stress relaxation due to the subsequent fracture initiations is indirectly captured by measuring the crack lengths and opening displacements from the 3D CT images at different loading steps. The stress relaxation is directly measured by DIC analysis using the macro-scale test data. DIC results show strains relaxed in the region between existing and emerging transverse cracks.

引用

页数：9

共 26 条

[1]

[Anonymous], 2017, OCT IM SOFTW VER 8

[2]

[Anonymous], 2017, AMIR SOFTW VER 6 2

[3]

Bale HA, 2013, NAT MATER, V12, P40, DOI [10.1038/nmat3497, 10.1038/NMAT3497]

[4] Characterization of SiC/SiC composites damage mechanisms using Digital Image Correlation at the tow scale [J].

Bernachy-Barbe, Fabien ;

Gelebart, Lionel ;

Bornert, Michel ;

Crepin, Jerome ;

Sauder, Cedric .

COMPOSITES PART A-APPLIED SCIENCE AND MANUFACTURING, 2015, 68 :101-109

[5] In Situ Experiments with X ray Tomography: an Attractive Tool for Experimental Mechanics [J].

Buffiere, J. -Y. ;

Maire, E. ;

Adrien, J. ;

Masse, J. -P. ;

Boller, E. .

EXPERIMENTAL MECHANICS, 2010, 50 (03) :289-305

[6] Microscopical observations of inter-fibre failure under tension [J].

Correa, Elena ;

Inmaculada Valverde, Maria ;

Luisa Velasco, Maria ;

Paris, Federico .

COMPOSITES SCIENCE AND TECHNOLOGY, 2018, 155 :213-220

[7] Local damage in a 5-harness satin weave composite under static tension: Part II - Meso-FE modelling [J].

Daggumati, S. ;

Van Paepegem, W. ;

Degrieck, J. ;

Xu, J. ;

Lomov, S. V. ;

Verpoest, I. .

COMPOSITES SCIENCE AND TECHNOLOGY, 2010, 70 (13) :1934-1941

[8] An experimental study of failure initiation and propagation in 2D woven composites under compression [J].

De Carvalho, N. V. ;

Pinho, S. T. ;

Robinson, P. .

COMPOSITES SCIENCE AND TECHNOLOGY, 2011, 71 (10) :1316-1325

[9]

Deloitte Touche Tohmatsu Limited, 2018, AUT COMP MAT CURR ST

[10]

Garcea SC, 2018, COMPOS SCI TECHNOL, V156, P305, DOI [10.1016/j.compscitech.2017.10.023, 10.22201/iij.24484881e.2018.38.11886]

← 1 2 3 →