Analysis of intermetallic layer in dissimilar TIG welding-brazing butt joint of aluminium alloy to stainless steel

被引:73
作者
Song, J. L. [1 ]
Lin, S. B. [1 ]
Yang, C. L. [1 ]
Fan, C. L. [1 ]
Ma, G. C. [1 ]
机构
[1] Harbin Inst Technol, State Key Lab Adv Welding Prod Technol, Sch Mat Sci & Engn, Harbin 150001, Peoples R China
基金
中国国家自然科学基金;
关键词
Aluminium-steel hybrid joint; TIG welding-brazing; Intermetallic layer; Phase identification; Mechanical properties; AL-SI; FE; MICROSTRUCTURE; STABILITY; BEHAVIOR; ELEMENTS; PHASES;
D O I
10.1179/136217110X12665048207610
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
Intermetallic layer of dissimilar tungsten inert gas welding-brazing butt joint of aluminium alloy/stainless steel has been studied. A visible unequal thickness intermetallic layer has formed in welded seam/steel interface, and the thickness of the whole layer is <10 mu m. The interface with Al-12Si filler metal consists of iota(5)-Al8Fe2Si layer in welded seam side and theta-(Al,Si)(13)Fe-4 layer in steel side with the hardness values of 1025 and 835 HV respectively, while the interface with Al-6Cu filler metal consists of theta-Al-13(Fe,Cu)(4) layer with the hardness of 645 HV. The average tensile strength of the joint with Al-12Si filler metal is 100-120 MPa, and the fracture occurs at theta-(Al,Si)(13)Fe-4 layer, while the joint with Al-6% Cu filler metal presents high crack resistance with tensile strength of 155-175 MPa, which reaches more than 50% of aluminium base metal strength.
引用
收藏
页码:213 / 218
页数:6
相关论文
共 25 条
[1]   How complex is the microstructure of AA2024-T3? [J].
Boag, A. ;
Hughes, A. E. ;
Wilson, N. C. ;
Torpy, A. ;
MacRae, C. M. ;
Glenn, A. M. ;
Muster, T. H. .
CORROSION SCIENCE, 2009, 51 (08) :1565-1568
[2]   Growth and surface morphology of hot-dip Al-Si on 9Cr-1Mo steel [J].
Chang, Yo-Yu ;
Cheng, Wei-Jen ;
Wang, Chaur-Jeng .
MATERIALS CHARACTERIZATION, 2009, 60 (02) :144-149
[3]   Preparation of the Al-Cu-Fe & Al-Fe-Si ternary intermetallic powders via a novel reaction ball milling technique [J].
Chen, D ;
Chen, ZH ;
Chen, JH ;
Huang, PY .
JOURNAL OF ALLOYS AND COMPOUNDS, 2004, 376 (1-2) :89-94
[4]   A thermodynamic description of the Al-Fe-Si system over the whole composition and temperature ranges via a hybrid approach of CALPHAD and key experiments [J].
Du, Yong ;
Schuster, Julius Clemens ;
Liu, Zi-Kui ;
Hu, Rongxiang ;
Nash, Philip ;
Sun, Weihua ;
Zhang, Weiwei ;
Wang, Jiong ;
Zhang, Lijun ;
Tang, Chengying ;
Zhu, Zhijun ;
Liu, Shuhong ;
Ouyang, Yifang ;
Zhang, Wenqing ;
Krendelsberger, Nataliya .
INTERMETALLICS, 2008, 16 (04) :554-570
[5]   Study of aluminium-copper-iron alloys: application for laser cladding [J].
Dubourg, L ;
Hlawka, F ;
Cornet, A .
SURFACE & COATINGS TECHNOLOGY, 2002, 151 :329-332
[6]   Investigation of intermetallics in hypoeutectic Al-Fe alloys by dissolution of the Al matrix [J].
Goulart, Pedro R. ;
Lazarine, Valentim B. ;
Leal, Claudenete V. ;
Spinelli, Jose E. ;
Cheung, Noe ;
Garcia, Amauri .
INTERMETALLICS, 2009, 17 (09) :753-761
[7]   Joining phenomena and joint strength of friction welded joint between pure aluminium and low carbon steel [J].
Kimura, M. ;
Ishii, H. ;
Kusaka, M. ;
Kaizu, K. ;
Fuji, A. .
SCIENCE AND TECHNOLOGY OF WELDING AND JOINING, 2009, 14 (05) :388-395
[8]   The stability of structures with icosahedral local order in Al-based alloys with transition metals [J].
Kiv, AE ;
Ezersky, VI ;
Talianker, MM .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2003, 352 (1-2) :100-104
[9]   Identification of intermetallic phases in a eutectic Al-Si casting alloy using electron backscatter diffraction pattern analysis [J].
Kral, MV ;
McIntyre, HR ;
Smillie, MJ .
SCRIPTA MATERIALIA, 2004, 51 (03) :215-219
[10]   Dissimilar friction stir spot welding of low carbon steel and Al-Mg alloy by formation of IMCs [J].
Lee, C. -Y. ;
Choi, D. -H. ;
Yeon, Y. -M. ;
Jung, S-B .
SCIENCE AND TECHNOLOGY OF WELDING AND JOINING, 2009, 14 (03) :216-220