Influence of aging pre-treatment on the compressive deformation of WE54 alloy

被引：38

作者：

Beladi, H. ^{[1
]}

Barnett, M. R. ^{[1
]}

机构：

[1] Deakin Univ, Ctr Mat & Fibre Innovat, Geelong, Vic 3217, Australia

来源：

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING | 2007年 / 452卷 / 306-312期

关键词：

age hardening; compressive deformation; twinning; slip; WE54; alloy;

D O I：

10.1016/j.msea.2006.10.125

中图分类号：

TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

The effect of aging pre-treatment on the compressive deformation of a commercial WE54 alloy is studied. Age hardening treatments were performed at 170 degrees C, 250 degrees C and 300 degrees C. Compression testing was then carried out for the peak aged samples at temperatures between ambient and 450 degrees C. Twinning dominated the deformation at lower temperatures for all initial microstructures. This behaviour was replaced by slip dominated flow when the temperature was raised. The temperature of the transition from twinning to slip dominated flow was only mildly sensitive to the pre-treatment. It is also evident that dynamic recrystallization is retarded in this alloy. (c) 2006 Elsevier B.V. All rights reserved.

引用

页码：306 / 312

页数：7

共 18 条

[1] Application of texture simulation to understanding mechanical behavior of Mg and solid solution alloys containing Li or Y [J].

Agnew, SR ;

Yoo, MH ;

Tomé, CN .

ACTA MATERIALIA, 2001, 49 (20) :4277-4289

[2]

AHMED M, 1992, MAGNESIUM ALLOYS AND THEIR APPLICATIONS, P301

[3] Influence of grain size on the compressive deformation of wrought Mg-3Al-1Zn [J].

Barnett, MR ;

Keshavarz, Z ;

Beer, AG ;

Atwell, D .

ACTA MATERIALIA, 2004, 52 (17) :5093-5103

[4] A Taylor model based description of the proof stress of magnesium AZ31 during hot working [J].

Barnett, MR .

METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2003, 34A (09) :1799-1806

[5]

BEER AG, 2004, THESIS DEAKIN U GEEL

[6]

DESCHAMPS A, 1999, P 7 SEM INT FED HEAT, P1

[7] Correlation of plastic deformation and dynamic recrystallization in magnesium alloy Zk60 [J].

Galiyev, A ;

Kaibyshev, R ;

Gottstein, G .

ACTA MATERIALIA, 2001, 49 (07) :1199-1207

[8]

Karimzadeh H., 1998, THESIS U MANCHESTER

[9]

KELLEY EW, 1968, T METALL SOC AIME, V242, P5

[10]

Lorimer G.W., 1986, P LOND C MAGN TECHN, P47

← 1 2 →