Microstructural response of polypropylene fibres at high temperature to protect concrete from spalling

被引：2

作者：

Alonso, M. C. ^{[1
]}

Flor-Laguna, V. ^{[1
]}

Sanchez, M. ^{[1
]}

机构：

[1] IETcc CSIC, Inst Construct Sci Eduardo Torroja, Madrid, Spain

来源：

CONCRETE SPALLING DUE TO FIRE EXPOSURE: PROCEEDINGS OF THE 3RD INTERNATIONAL WORKSHOP | 2013年 / 6卷

关键词：

HIGH-STRENGTH CONCRETE; PERFORMANCE; BEHAVIOR;

D O I：

10.1051/matecconf/20130602001

中图分类号：

TU [建筑科学];

学科分类号：

0813 ;

摘要：

The microstructural analysis of the interfacial transition zone (ITZ) and the interaction of polypropylene fibres (PPF) with mortar in the temperature region 170 to 300. C have been considered. The results confirm a mixed mechanism: The presence of the PPF alters the ITZ and favours an initial cracking formation. After melting, PPF diffuses in the surrounding cement paste closing micropores while, simultaneously, macro pores are increased as consequence of the free space leaved and the growing of microcracks.

引用

页数：7

共 16 条

[1] Dehydration and rehydration processes of cement paste exposed to high temperature environments [J].

Alonso, C ;

Fernandez, L .

JOURNAL OF MATERIALS SCIENCE, 2004, 39 (09) :3015-3024

[2]

Alonso C., 2005, ACI SP, P289

[3]

[Anonymous], 2010, MATERIALVERHALTEN HO

[4] Effect of fibre type and geometry on maximum pore pressures in fibre-reinforced high strength concrete at elevated temperatures [J].

Bangi, Mugume Rodgers ;

Horiguchi, Takashi .

CEMENT AND CONCRETE RESEARCH, 2012, 42 (02) :459-466

[5]

Bentz DP, 2000, ACI MATER J, V97, P351

[6]

BENTZ DP, 1991, CEMENT CONCRETE RES, V21, P324

[7] TIME-DEPENDENT STRESS IN POLYMER MELTS AND REVIEW OF VISCOELASTIC THEORY [J].

CHEN, IJ ;

BOGUE, DC .

TRANSACTIONS OF THE SOCIETY OF RHEOLOGY, 1972, 16 (01) :59-&

[8]

Haniche R., 2011, CONTRIBUTION ETUDE B

[9] High-temperature behaviour of HPC with polypropylene fibres -: From spalling to microstructure [J].

Kalifa, P ;

Chéné, G ;

Gallé, C .

CEMENT AND CONCRETE RESEARCH, 2001, 31 (10) :1487-1499

[10]

Klingsch E., 2011, 2 INT RILEM WS CONCR, P245

← 1 2 →