Fabrication of superhydrophobic Pt3Fe/Fe surface for its application

Well-defined Pt3Fe/Fe superhydrophobic materials on iron sheet with special properties, such as corrosion resistance, superhydrophobicity and superoleophilicity, was fabricated. The fabrication process involved etching in hydrochloric acid aqueous solution and simple replacement deposition process without using any seed and organic solvent, and then annealing. The electrochemical measurements show that the resultant surface in 3.5% sodium chloride solution displays good corrosion resistance. Also, it is proved that the obtained surface has better mechanical abrasion resistance via scratch test. The superoleophilicity and low water adhesion force of the obtained surface endow it high oil/water separation capacity. The as-prepared nanocomposites display enhanced catalytic activity and kinetics toward degradation of methyl orange. In particular, it possesses the most efficient degradation capacity (95%) towards methyl orange at a high concentration (17.5 mg/L) in 80 min. The improved stability and excellent catalytic activity of the Pt3Fe/Fe nanocomposites promise new opportunities for the development of waste water treatment.