Restoration of ductility in hydrogen embrittled dual-phase (DP 780) steel by the electric pulse treatment

被引:8
作者
Kumar, Anuranjan [1 ]
Paul, Surajit Kumar [1 ]
机构
[1] Indian Inst Technol Patna, Dept Mech Engn, Bihta, Patna 801106, India
来源
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING | 2022年 / 847卷
关键词
Hydrogen embrittlement; Centerline crack; Electric pulse treatment; Damage recovery; Dual-phase steel; ENHANCED LOCALIZED PLASTICITY; MECHANICAL-PROPERTIES; ASSISTED CRACKING; SHEET-METAL; BEHAVIOR; MARTENSITE; FRACTURE; MODEL; SUSCEPTIBILITY; IDENTIFICATION;
D O I
10.1016/j.msea.2022.143256
中图分类号
TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
High-strength steel components operating in a hydrogen environment are more susceptible to hydrogen embrittlement. De-hydrogenation of these components could prolong their service life, encouraging the industrial use of high-strength steel. In this study, hydrogen (H)-induced damage recovery and restoration of ductility are realized in dual-phase (DP 780) steel by the electric pulse treatment (EPT). The experimental results indicate that a complete restoration of ductility and H-induced damage recovery could be achieved with suitable electropulsing parameters in DP 780 steel. A centerline crack is observed in the fractographic examination of each hydrogenated specimen after the uniaxial tensile test. After EPT, post-necking ductility improves, and the centerline crack disappears from the fractured surface. The in-situ digital image correlation (DIC) technique is utilized during the uniaxial tensile test to measure the local strain evolution. Both uniaxial tensile necking and fracture strains are restored after EPT of hydrogenated specimens.
引用
收藏
页数:11
相关论文
共 63 条
[41]   A critical perspective on pipeline processing and failure risks in hydrogen service conditions [J].
Ohaeri, Enyinnaya G. ;
Qin, Wen ;
Szpunar, Jerzy .
JOURNAL OF ALLOYS AND COMPOUNDS, 2021, 857
[42]   DIFFUSION AND TRAPPING OF HYDROGEN IN STEEL [J].
ORIANI, RA .
ACTA METALLURGICA, 1970, 18 (01) :147-&
[43]   HYDROGEN EMBRITTLEMENT OF STEELS [J].
ORIANI, RA .
ANNUAL REVIEW OF MATERIALS SCIENCE, 1978, 8 :327-357
[44]  
ORIANI RA, 1972, BERICH BUNSEN GESELL, V76, P848
[45]   Controlling factors of forming limit curve: A review [J].
Paul, Surajit Kumar .
ADVANCES IN INDUSTRIAL AND MANUFACTURING ENGINEERING, 2021, 2
[46]   Identification of Post-necking Tensile Stress-Strain Behavior of Steel Sheet: An Experimental Investigation Using Digital Image Correlation Technique [J].
Paul, Surajit Kumar ;
Roy, Satish ;
Sivaprasad, S. ;
Bar, H. N. ;
Tarafder, S. .
JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2018, 27 (11) :5736-5743
[47]   CLASSIFICATION OF HYDROGEN TRAPS IN STEEL [J].
PRESSOUYRE, GM .
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1979, 10 (10) :1571-1573
[48]   The Impact of Nb, Ti, Zr, B, V, and Mo on the Hydrogen Diffusion in Four Different AHSS/UHSS Microstructures [J].
Rehrl, Johannes ;
Mraczek, Klemens ;
Pichler, Andreas ;
Werner, Ewald .
STEEL RESEARCH INTERNATIONAL, 2014, 85 (03) :336-346
[49]   Mechanical properties and fracture behavior of hydrogen charged AHSS/UHSS grades at high- and low strain rate tests [J].
Rehrl, Johannes ;
Mraczek, Klemens ;
Pichler, Andreas ;
Werner, Ewald .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2014, 590 :360-367
[50]   Factors affecting hydrogen-assisted cracking in a commercial tempered martensitic steel: Mn segregation, MnS, and the stress state around abnormal cracks [J].
Sasaki, Daisuke ;
Koyama, Motomichi ;
Noguchi, Hiroshi .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2015, 640 :72-81