Coatings made of tungsten carbide and tantalum carbide for machining tools

被引：13

作者：

Palomar, F. E. ^{[1
]}

Zambrano, P. C. ^{[1
]}

Gomez, M. I. ^{[2
]}

Colas, R. ^{[1
]}

Guerrero, M. P. ^{[1
]}

Castillo, A. ^{[1
]}

机构：

[1] Univ Autonoma Nuevo Leon, Fac Ingn Mecan & Elect, San Nicolas De Los Garza 66451, NL, Mexico

[2] Univ Autonoma Nuevo Leon, Fac Ciencias Quim, San Nicolas De Los Garza 66451, NL, Mexico

来源：

VACUUM | 2010年 / 84卷 / 10期

关键词：

Coated films; WC; TaC; Machining tools;

D O I：

10.1016/j.vacuum.2009.10.032

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Continuous evolution of cutting parameters has been a constant requirement for the manufacture of machining tools. This has promoted the development of new technologies to reduce the production time as well as cost without affecting the competitiveness. In the present work, high speed tools have been coated with WC and TaC by means of chemical vapour deposition and tested in a high speed milling machine. Damages on the tips of these cutting tools were analysed by scanning electron microscope. These observations show that the coating is heterogeneous and affected by the type and composition of various phases formed. Results indicate that the coating made from WC is more highly resistant to attrition than that made of TaC. Surfaces that have been machined by the coated tools are evaluated by means of the average roughness parameter (C) 2009 Elsevier Ltd. All rights reserved.

引用

页码：1236 / 1239

页数：4

共 11 条

[1] COLEMAN JR, 1984, TOOLING PRODUCTI MAY, P46
[2] The influence of the microstructure of three Al-Si alloys on the cutting-force amplitude during fine turning
Grum, J
Kisin, M
[J]. INTERNATIONAL JOURNAL OF MACHINE TOOLS & MANUFACTURE, 2006, 46 (7-8) : 769 - 781
[3] Adhesion and failure mechanisms of tungsten-carbon containing multilayered and graded coatings subjected to scratch tests
Harry, E
Rouzaud, A
Juliet, P
Pauleau, Y
[J]. THIN SOLID FILMS, 1999, 342 (1-2) : 207 - 213
[4] COMPACTION, DISTRIBUTION, AND CHEMICAL BONDING OF TUNGSTEN-IMPLANTED GLASSY-CARBON
HOFFMAN, A
EVANS, PJ
COHEN, DD
PATERSON, PJK
[J]. JOURNAL OF APPLIED PHYSICS, 1992, 72 (12) : 5687 - 5694
[5] JOHNE P, 1984, HDB ALUMINIUMZERSPAN
[6] QUINTO DT, 1998, 25 INT C MET COAT TH
[7] A REVIEW OF THE PRESENT STATE OF ART IN HARD COATINGS GROWN FROM THE VAPOR-PHASE
SUNDGREN, JE
HENTZELL, HTG
[J]. JOURNAL OF VACUUM SCIENCE & TECHNOLOGY A-VACUUM SURFACES AND FILMS, 1986, 4 (05): : 2259 - 2279
[8] Vincenzini P., 1987, HIGH TECH CERAMICS, P145
[9] YANG HY, 1646, J VAC SCI TECHNOL A, P6
[10] Hardness and morphological characterization of tungsten carbide thin films
Zambrano, G
Prieto, P
Perez, F
Rincon, C
Galindo, H
Cota-Araiza, L
Esteve, J
Martinez, E
[J]. SURFACE & COATINGS TECHNOLOGY, 1998, 108 (1-3) : 323 - 327

← 1 2 →