Technical and economical stainless steel alternatives for civil engineering applications

被引：11

作者：

Burkert, A. ^{[1
]}

Lehmann, J. ^{[1
]}

Burkert, A. ^{[1
]}

Mietz, J. ^{[1
]}

Guempel, P. ^{[2
]}

机构：

[1] BAM Fed Inst Mat Res & Testing, Div Corros Civil Engn 6 1, D-12205 Berlin, Germany

[2] Univ Appl Sci, Fac Mech Engn, Hsch Konstanz, D-78462 Constance, Germany

来源：

MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION | 2014年 / 65卷 / 11期

关键词：

STRESS-CORROSION CRACKING; RESISTANCE;

D O I：

10.1002/maco.201307057

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Systematic laboratory and field exposure tests allow to compare nine different stainless steels (three ferritic, three austenitic, and three duplex grades) for civil engineering applications. The influence of surface finish was also taken into account by choosing five different industry-specific features. The three duplex stainless steels revealed excellent corrosion resistance under most of the test conditions. Especially for applications in civil engineering the lean duplex steels offer distinct advantages. The manganese-alloyed 1.4376 and the ferritic steel 1.4509 cannot be recommended as alternative materials as they did not perform satisfactorily.

引用

页码：1080 / 1095

页数：16

共 24 条

[1]

[Anonymous], 10081200509 DIN EN

[2]

[Anonymous], 2004, DVGW ARB G 541 OKT 2

[3]

[Anonymous], 50018199706 DIN

[4]

[Anonymous], 102892001 DIN EN ISO

[5]

[Anonymous], 85651995 DIN EN ISO

[6]

[Anonymous], 92272006 DIN EN ISO

[7] STRESS-CORROSION CRACKING BEHAVIOR OF STAINLESS-STEELS WITH RESPECT TO THEIR USE IN ARCHITECTURE .2. CORROSION IN THE PASSIVE STATE [J].

ARLT, N ;

MICHEL, E ;

HIRSCHFELD, D ;

BUSCH, H ;

STELLFELD, I ;

GRIMME, D ;

STEINBECK, G .

STEEL RESEARCH, 1993, 64 (10) :526-533

[8]

Arlt N., 2001, KORROSION KORROSIONS, V2, p937ff

[9] Chloride induced corrosion on stainless steels at indoor swimming pools atmospheres .1. Electrolyte magnesium-chloride (30%) [J].

Arnold, N ;

Gumpel, P ;

Heitz, T ;

Pscheidl, P .

MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION, 1997, 48 (10) :679-686

[10]

Burkert A., 2011, SCHLUSSBERICHT ZUM A

← 1 2 3 →