SCC behaviours of austenitic stainless steel Z3CN20-09M in high temperature water

被引：4
|
作者：
Lu, Y. H. [1 ]
Chen, Z. R. [1 ]
Zhu, X. F. [1 ]
Shoji, T. [1 ,2 ]
机构：
[1] Univ Sci & Technol Beijing, Natl Ctr Mat Serv Safety, Beijing 100083, Peoples R China
[2] Tohoku Univ, New Ind Creat Hatchery Ctr, Frontier Res Initiat, Aoba Ku, Sendai, Miyagi 9808579, Japan
来源：
MATERIALS SCIENCE AND TECHNOLOGY | 2014年 / 30卷 / 15期
关键词：
Stainless steel; Stress corrosion cracking; Pitting corrosion; Intergranular corrosion; High temperature corrosion; Interfaces; STRESS-CORROSION CRACKING; PRESSURE-VESSEL; PURE WATER; GROWTH; ENVIRONMENT; BWR;
D O I：
10.1179/1743284714Y.0000000585
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Stress corrosion cracking (SCC) behaviours of Z3CN20-09M stainless steel in high temperature water containing Cl- were studied. The results indicated that SCC sensitivity was inconsistent with test temperature. The minimum and maximum of SCC sensitivity occurred at 320 and 290 degrees C respectively, and SCC sensitivity at 250 degrees C fell between them. SCC crack initiated preferentially at bottom of corrosion pit or along phase boundary between austenite and ferrite, and its propagation depended on relative orientation to the phase boundary. SCC crack parallel to the phase boundary propagated along the phase boundary, while that perpendicular to the phase boundary was hindered to propagate.
引用
收藏
页码：1944 / 1950
页数：7
相关论文
共 50 条
  • [1] Effect of test temperature on SCC behavior of Z3CN20-09M stainless steel in high temperature water containing chloride ions
    Lu, Yong-Hao
    Chen, Zi-Rui
    Zhu, Xiao-Feng
    Beijing Keji Daxue Xuebao/Journal of University of Science and Technology Beijing, 2013, 35 (10): : 1320 - 1326
  • [2] Effect of phase boundary on nucleation and propagation of microcrack in nuclear grade Z3CN20-09M stainless steel
    Lu, Y. H.
    Zhu, X. F.
    MATERIALS SCIENCE AND TECHNOLOGY, 2014, 30 (08) : 968 - 972
  • [3] THE MICROSTRUCTURE AND TENSILE FRACTURE BEHAVIOR OF LONG TERM THERMAL AGED Z3CN20-09M STAINLESS STEEL
    Zheng Kai
    Wang Yanli
    Li Shilei
    Lu Xuming
    Wang Xitao
    Xue Fei
    ACTA METALLURGICA SINICA, 2013, 49 (02) : 175 - 180
  • [4] Cavitation erosion and its effect on corrosion resistance of nuclear-grade Z3CN20-09M stainless steel
    Wang, Zhenhua
    Wang, Yuefeng
    MATERIALS & DESIGN, 2022, 221
  • [5] Effects of Hot Working on the Microstructure and Thermal Ageing Impact Fracture Behaviors of Z3CN20-09M Duplex Stainless Steel
    Zhang Hai
    Li Shilei
    Liu Gang
    Wang Yanli
    ACTA METALLURGICA SINICA, 2017, 53 (05) : 531 - 538
  • [6] Influence of Thermal Ageing and Specimen Size on Fracture Toughness of Z3CN20-09M Casting Duplex Stainless Steels
    Wang, Yu
    Yao, Yaohong
    Wang, Zhengpin
    Jin, Yaohua
    Gao, Yuyu
    Cao, Nan
    Liu, Jiangnan
    MATERIALS TRANSACTIONS, 2018, 59 (06) : 917 - 921
  • [7] The Microstructure and Mechanical and Corrosion Behaviors of Thermally Aged Z3CN20-09M Cast Stainless Steel for Primary Coolant Pipes of Nuclear Power Plants
    Xue, Fei
    Shi, Fangjie
    Zhang, Chuangju
    Zheng, Qiaoling
    Yi, Dawei
    Li, Xiuqing
    Li, Yefei
    COATINGS, 2021, 11 (08)
  • [8] EFFECTS OF THERMAL AGING ON MICRO-MECHANICAL PROPERTIES AND IMPACT FRACTURE BEHAVIOR OF Z3CN20-09M STAINLESS STEELS
    Li Shilei
    Wang Xitao
    Wang Yanli
    Li Shuxiao
    ACTA METALLURGICA SINICA, 2011, 47 (06) : 751 - 756
  • [9] 采用VOD工艺冶炼泵壳用钢Z3CN20-09M
    杨建春
    大型铸锻件, 2007, (05) : 38 - 39+43
  • [10] Z3CN20-09M钢高温高压水蒸气腐蚀行为研究
    王正品
    王静
    要玉宏
    金耀华
    王毓
    西安工业大学学报, 2016, 36 (04) : 310 - 316
12345