Atomic emission spectroelectrochemistry applied to dealloying phenomena II. Selective dissolution of iron and chromium during active-passive cycles of an austenitic stainless steel

被引:54
作者
Ogle, K. [1 ]
Mokaddem, M. [1 ]
Volovitch, P. [1 ]
机构
[1] Ecole Natl Super Chim Paris, CNRS, UMR7045, LPCS, F-75005 Paris, France
关键词
Stainless steel; Passivation; Selective dissolution; Iron-chromium alloys; Spectroelectrochemistry; FE-CR-ALLOYS; 0.5 M H2SO4; ANODIC-DISSOLUTION; ELECTRODE IMPEDANCES; REACTION MODEL; MECHANISM; RATES; FILMS; XPS;
D O I
10.1016/j.electacta.2009.08.028
中图分类号
O646 [电化学、电解、磁化学];
学科分类号
081704 ;
摘要
Atomic emission spectroelectrochemistry was used to investigate selective dissolution of a 304 austenitic stainless steel sample in 2M H(2)SO(4). The partial dissolution rates of Fe, Cr, Ni, Mn, Mo, and Cu were measured as function of time during a series of potentiostatic triggered activation/passivation cycles. When first exposed to sulfuric acid solution, the steel sample was in a passive state with a total steady state ionic dissolution rate expressed as an equivalent current density of 10 mu A cm(-2). A transition into the active and passive state could be triggered by cathodic (-700mV vs. Ag/AgCl) and anodic (+400 to +700mV vs. Ag/AgCl) potentiostatic pulses respectively of variable time. Excess Cr dissolution was observed during the activation cycle as compared to Fe and a depletion of Cr dissolution was observed during the passivation cycle. These results are interpreted in terms of the dissolution of a Cr rich passive layer during activation and selective dissolution of Fe, Mn, Ni and other elements to form a Cr rich passive layer during passivation. Quantitative analysis of the excess Cr showed that the residual film contained approximately 0.38 mu gCr/cm(2). Fe does not appear to be incorporated into the film at this early stage of passive film growth. Residual films of metallic nickel and copper were formed on the surface during the active period that subsequently dissolved during passivation. (C) 2009 Elsevier . All rights reserved.
引用
收藏
页码:913 / 921
页数:9
相关论文
共 19 条
[1]   The secondary passive film for type 304 stainless steel in 0.5 M H2SO4 [J].
Atrens, A ;
Baroux, B ;
Mantel, M .
JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1997, 144 (11) :3697-3704
[2]  
Bard AllenJ., 2001, ELECTROCHEMICAL METH, P808
[3]   THE APPLICATION OF ICP-MS AND XPS TO STUDIES OF ION SELECTIVITY DURING PASSIVATION OF STAINLESS-STEELS [J].
CASTLE, JE ;
QIU, JH .
JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1990, 137 (07) :2031-2038
[4]  
Clayton C.R., 1995, CorroszoHMecAaMzs/ms zw T/zeozy a#Zfraetzee, P175
[5]   Electronic structure study of ac modified passive film on stainless steel [J].
Du, TB .
BRITISH CORROSION JOURNAL, 2002, 37 (01) :18-22
[6]  
EPELBOIN I, 1979, CORROS SCI, V19, P1105, DOI 10.1016/S0010-938X(79)80099-2
[7]   Passivation of Fe-Cr alloys studied with ICP-AES and EQCM [J].
Hamm, D ;
Ogle, K ;
Olsson, COA ;
Weber, S ;
Landolt, D .
CORROSION SCIENCE, 2002, 44 (07) :1443-1456
[8]   DISSOLUTION RATES OF IRON AND CHROMIUM AND FE-CR-ALLOYS IN THE PASSIVE STATE [J].
HEINE, B ;
KIRCHHEIM, R .
CORROSION SCIENCE, 1990, 31 :533-538
[9]   MECHANISM OF ANODIC-DISSOLUTION OF IRON CHROMIUM-ALLOYS INVESTIGATED BY ELECTRODE IMPEDANCES .2. ELABORATION OF THE REACTION MODEL [J].
KEDDAM, M ;
MATTOS, OR ;
TAKENOUTI, H .
ELECTROCHIMICA ACTA, 1986, 31 (09) :1159-1165
[10]   MECHANISM OF ANODIC-DISSOLUTION OF IRON CHROMIUM-ALLOYS INVESTIGATED BY ELECTRODE IMPEDANCES .1. EXPERIMENTAL RESULTS AND REACTION MODEL [J].
KEDDAM, M ;
MATTOS, OR ;
TAKENOUTI, H .
ELECTROCHIMICA ACTA, 1986, 31 (09) :1147-1158