Improved EIS Analysis of the Electrochemical Behaviour of Carbon Steel in Alkaline Solution

被引：72

作者：

Chakri, S. ^{[1
]}

Frateur, I. ^{[1
]}

Orazem, M. E. ^{[2
]}

Sutter, E. M. M. ^{[1
]}

Tran, T. T. M. ^{[1
]}

Tribollet, B. ^{[1
]}

Vivier, V. ^{[1
]}

机构：

[1] UPMC Univ Paris 06, Sorbonne Univ, CNRS, Lab Interfaces & Syst Electrochim, 4 Pl Jussieu, F-75005 Paris, France

[2] Univ Florida, Dept Chem Engn, Gainesville, FL 32611 USA

来源：

ELECTROCHIMICA ACTA | 2017年 / 246卷

关键词：

Carbon steel; Complex-capacitance plot; Power-law model; Oxide film; Electrochemical impedance spectroscopy; PHASE-ELEMENT BEHAVIOR; IRON-OXIDE ELECTRODES; OXYGEN REDUCTION; STAINLESS-STEEL; RESISTIVITY DISTRIBUTIONS; IMPEDANCE SPECTROSCOPY; MILD-STEEL; CORROSION; PASSIVATION; MEDIA;

D O I：

10.1016/j.electacta.2017.06.096

中图分类号：

O646 [电化学、电解、磁化学];

学科分类号：

081704 ;

摘要：

Steady-state polarization curves, X-ray photoelectron spectroscopy, and impedance spectroscopy were used to explore the electrochemical properties for carbon steel in alkaline electrolytes. The complex-capacitance representation allowed determination of a capacitance value at high frequency, from which the oxide film thickness could be estimated. These results are in good agreement with values obtained using the power-law model, providing a single mathematical model that is shown to apply in both the anodic and cathodic domains for the characterization of an oxide layer. (C) 2017 Elsevier Ltd. All rights reserved.

引用

页码：924 / 930

页数：7

共 25 条

[21] Corrosion behavior of steel in simulated concrete pore solutions treated with calcium silicate hydrates [J].

Tang, Y. M. ;

Miao, Y. F. ;

Zuo, Y. ;

Zhang, G. D. ;

Wang, C. L. .

CONSTRUCTION AND BUILDING MATERIALS, 2012, 30 :252-256

[22] OXYGEN ELECTRO-REDUCTION ON IRON-OXIDE ELECTRODES .3. HETEROGENEOUS CATALYTIC H2O2 DECOMPOSITION [J].

VAGO, ER ;

CALVO, EJ .

JOURNAL OF ELECTROANALYTICAL CHEMISTRY, 1995, 388 (1-2) :161-165

[23] ELECTROCATALYSIS OF OXYGEN REDUCTION AT WELL-DEFINED IRON-OXIDE ELECTRODES [J].

VAGO, ER ;

CALVO, EJ ;

STRATMANN, M .

ELECTROCHIMICA ACTA, 1994, 39 (11-12) :1655-1659

[24] OXYGEN REDUCTION ON IRON .3. AN ANALYSIS OF THE ROTATING-DISK RING ELECTRODE MEASUREMENTS IN NEAR NEUTRAL SOLUTIONS [J].

ZECEVIC, S ;

DRAZIC, DM ;

GOJKOVIC, S .

JOURNAL OF ELECTROANALYTICAL CHEMISTRY, 1989, 265 (1-2) :179-193

[25] Effects of anodic passivation on the constitution, stability and resistance to corrosion of passive film formed on an Fe-24Mn-4Al-5Cr alloy [J].

Zhang, YS ;

Zhu, XM ;

Liu, M ;

Che, RX .

APPLIED SURFACE SCIENCE, 2004, 222 (1-4) :89-101

← 1 2 3 →