The influence of cooling rate on the microstructures and mechanical properties in ultrafine-grained aluminum processed by hot rolling

被引:8
作者
Sun, P. L. [1 ]
Zhao, Y. H. [2 ]
Tseng, T. Y. [3 ]
Su, J. R. [3 ]
Lavernia, E. J. [2 ]
机构
[1] Feng Chia Univ, Dept Mat Sci & Engn, Taichung 40724, Taiwan
[2] Univ Calif Davis, Dept Chem Engn & Mat Sci, Davis, CA 95616 USA
[3] China Steel Corp, New Mat Res & Dev Dept, Kaohsiung 81233, Taiwan
来源
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING | 2010年 / 527卷 / 20期
关键词
Ultrafine-grained aluminum; Hot and cold rolling; Cooling rate; Microstructures; Mechanical property; HIGH-TENSILE DUCTILITY; STACKING-FAULT ENERGY; THERMAL-STABILITY; NANOCRYSTALLINE FE; BOUNDARY STRUCTURE; DEFORMATION; STRENGTH; BEHAVIOR; GROWTH; SEGREGATION;
D O I
10.1016/j.msea.2010.04.087
中图分类号
TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
Commercially pure aluminum AA1050 was processed by hot rolling followed by subsequent water quenching (WQ) and furnace cooling (FC). The samples processed via these two approaches were then cold rolled to obtain ultrafine-grained (UFG) structures. Mechanical behavior studies showed that the WQ UFG Al exhibited a yield stress of 178 MPa and a total elongation of 5.3%, which are higher than those of the FC UFG Al (162 MPa and 3.1%, respectively). Microstructural analyses revealed that the origin of the high strength of the WQ UFG Al is attributable to smaller grain dimensions in the quenched and rolled material. The measured enhanced ductility was rationalized on the basis of three mechanisms: first, improved dislocation accumulation; second, a higher rate of strain hardening due to solid solution pinning during plastic deformation; and third, an increased proportion of high-angle grain boundaries. (C) 2010 Elsevier B.V. All rights reserved.
引用
收藏
页码:5287 / 5294
页数:8
相关论文
共 75 条
  • [1] Intermetallic phase selection in 1XXX Al alloys
    Allen, CM
    O'Reilly, KAQ
    Cantor, B
    Evans, PV
    [J]. PROGRESS IN MATERIALS SCIENCE, 1998, 43 (02) : 89 - 170
  • [2] Influence of stacking-fault energy on microstructural characteristics of ultrafine-grain copper and copper-zinc alloys
    Balogh, Levente
    Ungar, Tamas
    Zhao, Yonghao
    Zhu, Y. T.
    Horita, Zenji
    Xu, Cheng
    Langdon, Terence G.
    [J]. ACTA MATERIALIA, 2008, 56 (04) : 809 - 820
  • [3] GRAIN-GROWTH AND CHEMICAL ORDERING IN (FE,MN)(3)SI
    BANSAL, C
    GAO, ZQ
    FULTZ, B
    [J]. NANOSTRUCTURED MATERIALS, 1995, 5 (03): : 327 - 336
  • [4] Deformation induced grain boundaries in commercially pure aluminium
    Chang, CP
    Sun, PL
    Kao, PW
    [J]. ACTA MATERIALIA, 2000, 48 (13) : 3377 - 3385
  • [5] CHEN JH, 2007, THESIS NATL SUN YS U
  • [6] High ductility of ultrafine-grained steel via phase transformation
    Cheng, S.
    Choo, H.
    Zhao, Y. H.
    Wang, X-L.
    Zhu, Y. T.
    Wang, Y. D.
    Almer, J.
    Liaw, P. K.
    Jin, J. E.
    Lee, Y. K.
    [J]. JOURNAL OF MATERIALS RESEARCH, 2008, 23 (06) : 1578 - 1586
  • [7] Strength and tension/compression asymmetry in nanostructured and ultrafine-grain metals
    Cheng, S
    Spencer, JA
    Milligan, WW
    [J]. ACTA MATERIALIA, 2003, 51 (15) : 4505 - 4518
  • [8] High Plasticity and Substantial Deformation in Nanocrystalline NiFe Alloys Under Dynamic Loading
    Cheng, Sheng
    Zhao, Yonghao
    Guo, Yazhou
    Li, Ying
    Wei, Qiuming
    Wang, Xun-Li
    Ren, Yang
    Liaw, Peter K.
    Choo, Hahn
    Lavernia, Enrique J.
    [J]. ADVANCED MATERIALS, 2009, 21 (48) : 5001 - +
  • [9] Effect of Ppm level dopant on ductility of ultrafine grained gold wires
    Chew E.
    Kim H.H.
    Ferraris C.
    Zhao Y.H.
    Lavernia E.J.
    Wong C.C.
    [J]. Materials Science Forum, 2010, 633-634 : 449 - 457
  • [10] Dieter G.E., 1988, Mech. Metall, P289