A study on the re-solution heat treatment of AA 2618 aluminum alloy

被引：43
作者：
Ozbek, Ibrahim [1 ]
机构：
[1] Sakarya Univ, Sakarya Vocat High Sch, Sakarya MYO, Dept Met & Mat, TR-54200 Sakarya, Turkey
来源：
MATERIALS CHARACTERIZATION | 2007年 / 58卷 / 03期
关键词：
2618 aluminum alloy; age hardening; solution heat treatment; recrystallisation;
D O I：
10.1016/j.matchar.2006.07.002
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
In the present study, the effects of re-solution treatment of AA2618 aluminum alloy has been investigated. Solution heat treatments of 520-640 degrees C for 14-24 h were applied followed by artificial aging. Characterization studies that were carried out by optical microscopy, scanning electron microscopy and energy dispersive X-ray spectroscopy techniques showed that recrystallisation was not observed by solution treatment at 530 degrees C whereas it did occur as the solution treatment and the duration time were increased above 530 degrees C. Increasing the solution treatment temperature further coarsened both the grains and the precipitates, resulting in significant reduction in hardness. Al9FeNi-type intermetallics are not completely dissolved by these solution treatments. (c) 2006 Elsevier Inc. All rights reserved.
引用
收藏
页码：312 / 317
页数：6
相关论文
共 9 条
[1]  
Cavaliere P., 2002, J LIGHT METALS, V2, P247
[2]  
GILMAN PS, 1988, P DISPERSION STRENGT, P631
[3]  
Merchant HD, 1987, P HOM ANN AL COPP AL, P1
[4]  
POLMEAR IJ, 1981, LIGHT ALLOYS METALLU, P73
[5]   AA2618 and AA7075 alloys superplastic transition in isothermal hot-deformation tests [J].
Testani, C ;
Ielpo, FM ;
Alunni, E .
MATERIALS & DESIGN, 2000, 21 (04) :305-310
[6]   Progress in structural materials for aerospace systems [J].
Williams, JC ;
Starke, EA .
ACTA MATERIALIA, 2003, 51 (19) :5775-5799
[7]  
YOUDELIS WV, 1994, MATER SCI TECH SER, V10, P1031, DOI 10.1179/026708394790163627
[8]   Mechanical properties and microstructure of aluminum alloy 2618 with Al3(Sc, Zr) phases [J].
Yu, K ;
Li, WX ;
Li, SR ;
Zhao, J .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2004, 368 (1-2) :88-93
[9]  
1979, METALS HDB, V2, P81
1