Interlaminar interface relaxation upon heating carbon fiber thermoplastic-matrix composite, studied by contact electrical resistivity measurement

被引：9
作者：
Guerrero, VH [1 ]
Chung, DDL [1 ]
机构：
[1] SUNY Buffalo, Composite Mat Res Lab, Buffalo, NY 14260 USA
来源：
COMPOSITE INTERFACES | 2002年 / 9卷 / 06期
关键词：
composite; polymer; thermoplastic; nylon; carbon fiber; electrical resistivity; contact resistivity; interlaminar;
D O I：
10.1163/15685540260494128
中图分类号：
TB33 [复合材料];
学科分类号：
摘要：
The interlaminar interface of a crossply carbon fiber thermoplastic-matrix composite was found to relax upon heating at and above the glass transition temperature of the matrix. The relaxation caused the contact electrical resistivity of the interface to increase gradually and irreversibly.
引用
收藏
页码：557 / 563
页数：7
相关论文
共 13 条
[1]  
ALLIX O, 1994, DAMAGE MECH COMPOSIT, V185, P21
[2]  
ASTM International, 1995, D234484 ASTM, P43
[3]   Thermal analysis of carbon fiber polymer-matrix composites by electrical resistance measurement [J].
Chung, DDL .
THERMOCHIMICA ACTA, 2000, 364 (1-2) :121-132
[4]   DAMAGE-INDUCED PROPERTY CHANGES IN COMPOSITES SUBJECTED TO CYCLIC THERMAL LOADING [J].
HERAKOVICH, CT ;
HYER, MW .
ENGINEERING FRACTURE MECHANICS, 1986, 25 (5-6) :779-&
[5]   Effect of temperature on the transverse cracking behavior of cross-ply composite laminates [J].
Huang, X ;
Gillespie, JW ;
Eduljee, RF .
COMPOSITES PART B-ENGINEERING, 1997, 28 (04) :419-424
[6]  
IYER SL, 1989, P 34 INT SAMPE S COV, P2172
[7]  
Mei Z, 2000, POLYM POLYM COMPOS, V8, P319
[8]   Thermal history of carbon-fiber polymer-matrix composite, evaluated by electrical resistance measurement [J].
Mei, Z ;
Chung, DDL .
THERMOCHIMICA ACTA, 2001, 369 (1-2) :87-93
[9]  
Wang SK, 1999, COMPOS INTERFACE, V6, P497
[10]   Interlaminar damage in carbon fiber polymer-matrix composites, studied by electrical resistance measurement [J].
Wang, SK ;
Mei, Z ;
Chung, DDL .
INTERNATIONAL JOURNAL OF ADHESION AND ADHESIVES, 2001, 21 (06) :465-471
12