High temperature abrasive wear behavior of an as-cast ductile iron

被引：31

作者：

Celik, O ^{[1
]}

Ahlatci, H ^{[1
]}

Kayali, ES ^{[1
]}

Cimenoglu, H ^{[1
]}

机构：

[1] Istanbul Tech Univ, Dept Met & Mat Engn, TR-34469 Istanbul, Turkey

来源：

WEAR | 2005年 / 258卷 / 1-4期

关键词：

abrasion; ductile iron; high temperature; strain aging; tensile test; wear;

D O I：

10.1016/j.wear.2004.09.004

中图分类号：

TH [机械、仪表工业];

学科分类号：

0802 ;

摘要：

In this study, high temperature abrasive wear behavior of a GGG 40 quality as-cast ductile iron was examined. Wear tests were performed under a compression stress of 5.7 N/mm(2), by rubbing the samples (pins) on Al2O3 abrasive grains at various temperatures in between 25 and 600degreesC. The examined ductile iron exhibited the highest resistance to abrasion at temperature range between 50 and 100degreesC. Tensile tests carried out at 100degreesC revealed occurrence of serrated flow on the stress-strain curve, which is the indication of strain aging. (C) 2004 Elsevier B.V. All rights reserved.

引用

页码：189 / 193

页数：5

共 10 条

[1]

*ASM, 1996, ASM SPEC HDB CAST IR, P452

[2]

BAYDOGAN M, 1999, STEELS MAT POWER PLA, V7, P219

[3]

Ceilik O, 2003, ISIJ INT, V43, P1274

[4]

CELIK O, 2001, THESIS ITU I SCI TEC

[5]

Hutchings I.M., 1992, TRIBOLOGY FRICTION W, P156

[6] HIGH-TEMPERATURE PROPERTIES OF FERRITIC SPHEROIDAL GRAPHITE CAST-IRON [J].

LUI, TS ;

CHAO, CG .

JOURNAL OF MATERIALS SCIENCE, 1989, 24 (07) :2503-2507

[7] EFFECTS OF MICROSTRUCTURES ON THE ABRASIVE WEAR BEHAVIOR OF SPHEROIDAL CAST-IRON [J].

LUO, QS ;

XIE, JP ;

SONG, YP .

WEAR, 1995, 184 (01) :1-10

[8]

MEYERS MA, 1984, MECHANICAL METALLURG, P399

[9] DYNAMIC STRAIN AGING OF VARIOUS STEELS [J].

SACHDEV, AK .

METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1982, 13 (10) :1793-1797

[10] TENSILE CHARACTERISTICS OF AUSTEMPERED DUCTILE CAST-IRON IN THE TEMPERATURE REGIME OF 300 K TO 693 K [J].

SHIEH, CS ;

LUI, TS ;

CHEN, LH .

MATERIALS TRANSACTIONS JIM, 1995, 36 (05) :620-625

← 1 →