Nanocrystalline Gd1-xCaxFeO3 sensors for detection of methanol gas

被引：28

作者：

Wang Xiaofeng ^{[1
]}

Ma Wei ^{[1
]}

Sun Kaiming ^{[1
]}

Hu Jifan ^{[2
]}

Qin Hongwei ^{[2
]}

机构：

[1] Dalian Univ Technol, Sch Math & Phys Sci, Panjin 124221, Peoples R China

[2] Shandong Univ, Sch Phys, State Key Lab Crystal Mat, Jinan 250100, Shandong, Peoples R China

来源：

JOURNAL OF RARE EARTHS | 2017年 / 35卷 / 07期

基金：

中国国家自然科学基金;

关键词：

gas sensor; methanol; electrical properties; perovskite; rare earths; CO-SENSING PROPERTIES; FE-O PEROVSKITE; THIN-FILMS; ETHANOL; OXIDE; SENSITIVITY; CATALYSTS; SURFACE;

D O I：

10.1016/S1002-0721(17)60965-7

中图分类号：

O69 [应用化学];

学科分类号：

081704 ;

摘要：

The sol-gel method was used to prepare the nanocrystalline Gd1-xCaxFeO3 (x=0-0.4) powders. The XRD results showed that all the Gd1-xCaxFeO3 (x=0-0.4) compounds crystallized as perovskite phase with orthorhombic structure. The doping of Ca in GdFeO3 not only reduced the resistance, but also enhanced the response to methanol. The Gd0.9Ca0.1FeO3 showed the best response to methanol among Gd1-xCaxFeO3 sensors. Besides, it showed good selectivity to methanol among methanol, ethanol, CO and formaldehyde gases. The responses at 260 degrees C for Gd0.9Ca0.1FeO3-based sensor to 600 ppm methanol, ethanol and CO gases were 117.7, 72.7 and 31.9, respectively. Even at quite low gas concentrations, Gd0.9Ca0.1FeO3-based sensor had an obvious response. At 260 degrees C, the response of 1.54 was obtained to be 45 ppm methanol. The experimental results showed that nanocrystalline Gd0.9Ca0.1FeO3 based sensor can be used to detect methanol gas.

引用

页码：690 / 696

页数：7

共 43 条

[1] PHYSICOCHEMICAL PROPERTIES OF RARE-EARTH PEROVSKITE OXIDES USED AS GAS SENSOR MATERIAL [J].

ARAKAWA, T ;

KURACHI, H ;

SHIOKAWA, J .

JOURNAL OF MATERIALS SCIENCE, 1985, 20 (04) :1207-1210

[2] CO/HC sensors based on thin films of LaCoO3 and La0.8Sr0.2CoO3-δ metal oxides [J].

Brosha, EL ;

Mukundan, R ;

Brown, DR ;

Garzon, FH ;

Visser, JH ;

Zanini, M ;

Zhou, Z ;

Logothetis, EM .

SENSORS AND ACTUATORS B-CHEMICAL, 2000, 69 (1-2) :171-182

[3] Array of thick film sensors for atmospheric pollutant monitoring [J].

Carotta, MC ;

Martinelli, G ;

Crema, L ;

Gallana, M ;

Merli, M ;

Ghiotti, G ;

Traversa, E .

SENSORS AND ACTUATORS B-CHEMICAL, 2000, 68 (1-3) :1-8

[4] Gas-sensitive electrical properties of perovskite-type SmFeO3 thick films [J].

Carotta, MC ;

Martinelli, G ;

Sadaoka, Y ;

Nunziante, P ;

Traversa, E .

SENSORS AND ACTUATORS B-CHEMICAL, 1998, 48 (1-3) :270-276

[5] Synthesis of La0.8Sr0.2Co0.5Ni0.5O3-δ thin films for high sensitivity CO sensing material using the Pechini process [J].

Chai, YL ;

Ray, DT ;

Chen, GJ ;

Chang, YH .

JOURNAL OF ALLOYS AND COMPOUNDS, 2002, 333 (1-2) :147-153

[6] Ethanol-sensing properties of SmFe1-xNixO3 perovskite oxides [J].

Chen, Linfu ;

Hu, Jifan ;

Fang, Shaoming ;

Han, Zhouxiang ;

Zhao, Ma ;

Wu, Zhanlei ;

Liu, Xing ;

Qin, Hongwei .

SENSORS AND ACTUATORS B-CHEMICAL, 2009, 139 (02) :407-410

[7] The influence of microstructure and deposition methods on CO gas sensing properties of La0.8Sr0.2Co1-xNixO3-δ perovskite films [J].

Chiu, CM ;

Chang, YH .

SENSORS AND ACTUATORS B-CHEMICAL, 1999, 54 (03) :236-242

[8] The structure, electrical and sensing properties for CO of the La0.8Sr0.2Co1-xNixO3-δ system [J].

Chiu, CM ;

Chang, YH .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1999, 266 (1-2) :93-98

[9] Sensitivity enhancement towards ethanol and methanol of TiO2 films doped with Pt and Nb [J].

Comini, E ;

Faglia, G ;

Sberveglieri, G ;

Li, YX ;

Wlodarski, W ;

Ghantasala, MK .

SENSORS AND ACTUATORS B-CHEMICAL, 2000, 64 (1-3) :169-174

[10] CO2 and O2 sensing behavior of nanostructured barium-doped SMCoO3 [J].

Delgado, E ;

Michel, CR .

MATERIALS LETTERS, 2006, 60 (13-14) :1613-1616

← 1 2 3 4 5 →