Reduction behavior and kinetics of vanadium-titanium sinters under high potential oxygen enriched pulverized coal injection

被引:7
作者
Ma, Jin-fang [1 ]
Wang, Guang-wei [1 ]
Zhang, Jian-liang [1 ]
Li, Xin-yu [2 ]
Liu, Zheng-jian [1 ]
Jiao, Ke-xin [1 ]
Guo, Jian [1 ]
机构
[1] Univ Sci & Technol Beijing, Sch Met & Ecol Engn, Beijing 100083, Peoples R China
[2] Wanbao Min Ltd, Plans & Operat Dept, Beijing 100053, Peoples R China
关键词
ore reduction; sintering; oxygen enrichment; pulverized coal; injection; kinetic models; MODEL; CHROMIUM; MGO;
D O I
10.1007/s12613-017-1430-5
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
In this work, the reduction behavior of vanadium-titanium sinters was studied under five different sets of conditions of pulverized coal injection with oxygen enrichment. The modified random pore model was established to analyze the reduction kinetics. The results show that the reduction rate of sinters was accelerated by an increase of CO and H-2 contents. Meanwhile, with the increase in CO and H-2 contents, the increasing range of the medium reduction index (MRE) of sinters decreased. The increasing oxygen enrichment ratio played a diminishing role in improving the reduction behavior of the sinters. The reducing process kinetic parameters were solved using the modified random role model. The results indicated that, with increasing oxygen enrichment, the contents of CO and H-2 in the reducing gas increased. The reduction activation energy of the sinters decreased to between 20.4 and 23.2 kJ/mol.
引用
收藏
页码:493 / 503
页数:11
相关论文
共 26 条
[1]   Increase of pulverized coal use efficiency in blast furnace [J].
Babich, A ;
Yaroshevskii, S ;
Formoso, A ;
Isidro, A ;
Ferreira, S ;
Cores, A ;
Garcia, L .
ISIJ INTERNATIONAL, 1996, 36 (10) :1250-1258
[2]  
Bai Y.Q., 2011, SINTERING PELLETIZIN, V36, P1
[3]  
Deng C.S., 1985, SICHUAN METALL, P4
[4]   Sustainable development of primary steelmaking under novel blast furnace operation and injection of different reducing agents [J].
Ghanbari, Hamid ;
Pettersson, Frank ;
Saxen, Henrik .
CHEMICAL ENGINEERING SCIENCE, 2015, 129 :208-222
[5]  
Hao Z., 2000, J IRON STEEL RES INT, V12, P81, DOI [10.13228/j.boyuan.issn1001-0963.2000.s1.018, DOI 10.13228/J.BOYUAN.ISSN1001-0963.2000.S1.018]
[6]  
Hu J.G., 2008, RES IRON STEEL, V36, P25
[7]  
Hu X.P., 2010, RES IRON STEEL, V38, P17
[8]  
Kasaoka S., 1985, International Chemical Engineering, V25, P160
[9]  
Li H.G., 2006, MAO EC STALINIZATION, P41
[10]  
Li Jia-xin, 2009, Journal of Iron and Steel Research, V21, P13